Precipitation Behavior Of (Nb, Ti)C In Coiling Process And Its Effect On Micro-Mechanical Characteristics Of Ferrite

Xu Yang,Sun Mingxue,Zhou Yanlei,Liu Zhenyu
DOI: https://doi.org/10.11900/0412.1961.2014.00265
IF: 1.797
2015-01-01
ACTA METALLURGICA SINICA
Abstract:High strength micro-alloyed steel has been widely used in automobile and machines because of the remarkable high strength and forming property which are attributed to nano-precipitates and refinement of the organization. Since the nano-precipitates are mostly nucleated between austenite/ferrite transition and ferrite can significantly advance strength, it is important to investigate precipitate behavior in coiling process. Nanoindentation technology provides a chance to study the special influence of nano-precipitates on the micro-properties of ferrite. The effect of cooling rate during continuous cooling process and coiling process on microstructural evolution and micro-hardness of Nb-Ti micro-alloyed steel were studied by using the thermal mechanical simulator, micro-hardness instrument, TEM and nanoindentation instrument. The precipitate behaviors of (Nb,Ti)C in coiling process and its effect on nano-hardnesss of ferrite were discussed. Experiments results indicated that the increase of cooling rate in continuous cooling process and coiling process could promote the microstructure transition from ferrite and pearlite to bainite. The micro-hardness of the tested steel increased with the increase of cooling rate in continuous cooling process, and decreased with the cooling rate in coiling process because of the large number of the dispersive nano-precipitate in ferrite which could improve the strength of matrix. The smaller cooling rate could promote volume fraction of (Nb, Ti)C particles in ferrite because there was enough time for the nucleation and growth of (Nb, Ti)C precipitates. When the cooling rate in coiling process was 0.1 degrees C/s, precipitates were dispersive in ferrite matrix with a diameter of less than 10 nm. The nanohardness and Young's modulus of ferrite were 4.13 and 249.3 GPa for Nb-Ti micro-alloyed steel, 2.64 and 237.4 GPa for C-Si-Mn steel. The contribution of nano-precipitates to nanohardness of ferrite reached 1.49 GPa.
What problem does this paper attempt to address?