Effect of Hot Coiling Under Accelerated Cooling on Development of Non-equiaxed Ferrite in Low Carbon Steel

H. A. Lanjewar,Pranavkumar Tripathi

DOI: https://doi.org/10.1007/s11665-016-2065-9

IF: 2.3

2016-04-22

Journal of Materials Engineering and Performance

Abstract:Strengthening mechanisms dominant in non-equiaxed ferrite structures are not so familiar and well measured. In present study, non-equiaxed ferritic structures were generated and perceived to be strengthened by grain/crystal refinement, presence of varying substructures, solid solution strengthening, and textural hardening. A Nb-V microalloyed steel was modeled under various accelerated cooling and coiling temperature conditions in a thermo-mechanical simulator. Decrease in coiling temperature in conjunction with accelerated cooling resulted in non-equiaxed ferrite structures with array of phase morphologies. Intermediate transformation conditions produced increase in strength concurrent with observed smallness in crystallite size and high amount of microstrain in the matrix phase indicative of high dislocation densities and crystal imperfections. Increase in strength is partially attributed to solid solution and texture hardening owing to increase in (111) pole intensity in structure.

materials science, multidisciplinary