Abstract:The oxidation of Fe-36Ni invar alloy at 1273–1473 K in 15%CO2-(0, 3, 5, 6)%O2-N2 atmosphere and the effect of the grain structure on the compressed cracks were investigated using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), X-ray diffraction (XRD) and a microcomputer control universal material testing machine. The results showed that the oxygen content and the oxidation temperature had an obvious influence on the morphology of the external scales, which changed into only two-layer structures from three stratified structures when the oxygen content was 0% or the oxidation temperature was below or equal 1423 K. However, the subscales still consisted of a typical structure of the intergranular subscale and the intragranular subscale with different oxygen contents or oxidation temperatures. The growth rate of the scales did not depend on the partial pressure of oxygen when oxygen existed. The oxidation temperature had an obvious influence on the growth rate of the scales, the growth rate of the scales was slower below or equal 1423 K and faster over 1423 K. A linear relationship existed between the thickness of the scales and the square root of oxidation time, moreover, the estimated activation energy for the growth of the external scale, the intragranular scale and the intergranular scale were 165, 159 and 131 kJ/mol, respectively. The higher apparent activation energy corresponded to the thinner scale at each oxidation temperature. In addition, the compressed cracks were hard to propagate and grow in the specimen with equiaxed grain structures, which would result in the narrower and shallower compressed cracks and the better surface quality during the compressed process after oxidation.

Pre-oxidation Effect on Oxidation Behavior of F91 in Carbon Dioxide at 550 °C

Coordination of Pre-oxidation Time and Temperature for a Better Corrosion Resistance to CO2 at 550 °C

Effect of CO2 Gas Pressure on Composition, Growth Rate, and Structure of Duplex Oxide Formed on 9cr Steel at 550 °C

Carbon depositions within the oxide scale and its effect on the oxidation behavior of low alloy steel in low (0.1 MPa), sub-(5 MPa) and supercritical (10 MPa) CO2 at 550°C

Effect of Atmosphere on Duplex Oxide Formed on 9cr Steel at 550 °C

Oxidation Behavior and Lifetime Prediction of Three Commercial Alloys Used in Power Plants at 550 °C in CO2 Environment

Comparison of Microstructural Evolution of Oxides Formed on F91 Martensitic Steel Upon Breakaway Oxidation at 700 °C in Air and CO2

Improve Oxidation Resistance at High Temperature by Nanocrystalline Surface Layer.

Effect of Al2O3 scales from pre-oxidation on the microstructural evolution and phase transition of NiAlHf coatings at 1200 °C

Experimental Investigation of the Initial Stage of the Oxidation Mechanism of Co Coating for Solid Oxide Fuel Cell Interconnects at 650 °C

Pre-oxidation of porous ferritic Fe22Cr alloys for lifespan extension at high-temperature

Effect of surface finishing on the oxidation characteristics of a Fe-21Cr-32Ni alloy in supercritical carbon dioxide

Effect of Grain Size on the Oxidation of Fe–13Cr–5Ni Alloy at 973K in Ar–21vol%O2

Thermodynamic Analysis of Typical Alloy Oxidation and Carburization in High-Temperature CO2 Atmosphere

High-Temperature Oxidation Behavior of CrMoV, F91 and Mar-M247 Superalloys Exposed to Laboratory Air at 550 °C

Effect of Pre-Oxidation Treatment on Corrosion Resistance of FeCoSiBPC Amorphous Alloy

Temperature dependence of carbon deposits within oxide scale on CrMoV steel in atmospheric and supercritical CO2

Corrosion behavior of heat-resistant steel T91 in high-temperature supercritical carbon dioxide with impurity O2, SO2 or H2S

Effect of Pre-Oxidation on the Hot Corrosion of CoNiCrAlYRe Alloy

The oxidation of an equimolar FeCoNiAl medium-entropy alloy at 900 °C in various oxygen pressures

Influence of Heating Conditions on the Oxidation Behavior of Fe-36ni Invar Alloy