Abstract:This study investigates corrosion of Fe–Ni-based alloy 800H that were exposed to supercritical CO2 (sCO2), ambient air and argon gas at pressures up to 20 MPa, at 650 and 750 °C for up to 1000 h. This alloy and other comparable metal alloys are expected to be used in sCO2 heat exchanger cycles as proposed in the DOE Advanced Ultra-Supercritical program. Alloy 800H is considered for this application, because it meets the high-temperature strength and creep rupture requirements and is a lower cost alternative to other Ni-based alloys. The oxidation performance and microstructural changes due to exposure in sCO2 have been evaluated and compared with exposures in air and Ar. The 800H alloy showed similar oxide scale thicknesses in sCO2 as in air. A recrystallized zone was observed beneath the oxide formed in air and sCO2. No such zone was observed after exposure to Ar, suggesting this recrystallization was associated with the oxidation process and not simply an effect of surface finishing. A wider recrystallized zone was observed underneath the oxide formed in sCO2 than in air. The effect of air and sCO2 on internal oxidation and carburization was investigated as well, showing that air led to more internal oxidation but less internal carburization than sCO2. It was concluded that the carbon species provided by the sCO2 atmosphere in conjunction with the increased grain boundary density in the recrystallized zone allowed for more ingress of carbon into the base metal, which resulted in a higher densities of carbides beneath the oxide scale.

Comparison of Microstructural Evolution of Oxides Formed on F91 Martensitic Steel Upon Breakaway Oxidation at 700 °C in Air and CO2

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Study on Corrosion Characteristics of Heat-resistant Materials in Supercritical Carbon Dioxide Environment Containing Oxygen Impurities

Carbon depositions within the oxide scale and its effect on the oxidation behavior of low alloy steel in low (0.1 MPa), sub-(5 MPa) and supercritical (10 MPa) CO2 at 550°C

Effect of Atmosphere on Duplex Oxide Formed on 9cr Steel at 550 °C

Pre-oxidation Effect on Oxidation Behavior of F91 in Carbon Dioxide at 550 °C

Microstructure Evolution and Failure Mechanism of Cr-coated Zry-4 in Air and Steam at 1200 °C

Temperature dependence of carbon deposits within oxide scale on CrMoV steel in atmospheric and supercritical CO2

Effect of CO2 Gas Pressure on Composition, Growth Rate, and Structure of Duplex Oxide Formed on 9cr Steel at 550 °C

Oxidation After Breakdown of the Chromium-Rich Scale on Stainless Steels at High Temperature: Internal Oxidation

Oxidation Behavior and Lifetime Prediction of Three Commercial Alloys Used in Power Plants at 550 °C in CO2 Environment

High-Temperature Oxidation Behavior of CrMoV, F91 and Mar-M247 Superalloys Exposed to Laboratory Air at 550 °C

Thermodynamic Analysis of Typical Alloy Oxidation and Carburization in High-Temperature CO2 Atmosphere

Effects of Corrosion in Supercritical CO2 on the Microstructural Evolution in 800H Alloy

Experimental Investigation of the Initial Stage of the Oxidation Mechanism of Co Coating for Solid Oxide Fuel Cell Interconnects at 650 °C

Corrosion and Mechanical Performance of Grade 92 Ferritic-Martensitic Steel After Exposure to Supercritical Carbon Dioxide

Comparative Study On Oxidation Behavior Of Fe-5wt% Cr Alloy In Various Mixed Atmospheres At 900-1000 Degrees C

Coordination of Pre-oxidation Time and Temperature for a Better Corrosion Resistance to CO2 at 550 °C

Microstructural evolution of early-stage oxide film on 15–15Ti austenitic stainless steel under 500 °C steam

Oxidation behavior of two austenitic steels used in 600 ℃ supercritical coal-fired power plants

Comparative Study on Oxidation Behavior of Fe-5wt% Cr Alloy in Various Mixed Atmospheres at 900–1 000 °C