Tunable wettability of jet electrodeposited micro-nano structures modified by laser radiation
Ya Chen,Junwei Xu,Lida Shen,Jiantao Zhao,Jinsong Chen,Youwen Yang,Lin Wang,Jianfeng Zhao,Changjiang Wang
DOI: https://doi.org/10.1016/j.surfcoat.2022.128763
IF: 4.865
2022-09-25
Surface and Coatings Technology
Abstract:In this paper, the wettability contrast surfaces were prepared via modifier-free composite processing. Nickel particles were added in electrolytes to fabricate micro-nano hierarchical structures by magnetic field induced jet electrodeposition. Laser surface modification was used to selectively draw patterns on the coating surface. After aging in the air for 25 days, the coatings prepared by magnetic field induced jet electrodeposition exhibited superhydrophobic, and the patterns achieved hydrophilicity or hydrophobicity by different laser fluences. Moreover, the morphologies and chemical composition of micro-nano hierarchical structures were changed by different laser fluences. Micro melted spots and hydrophilic nickel oxide appeared on the coating surface after laser surface modification. The wettability of the coating was altered by hydrophobic nickel hydroxide hydroxylated from NiO and organic substances from the air. However, the micro-nano structures were damaged by laser surface modification and cannot adsorb organic substances from the air. In addition, the superhydrophobic coatings and the hydrophilic patterns were corrosion-resistant. Ecorr and jcorr were −0.2607 V and 7.225 × 10−6 A/cm2, −0.5078 V and 9.354 × 10−6 A/cm2, respectively. Thus, the modifier-free processing, which combines magnetic field induced jet electrodeposition and laser surface modification, offers potential in the areas of green preparation for wettability contrast surfaces.
physics, applied,materials science, coatings & films