Abstract:In recent years, inspired by “biomimicry”, superhydrophobic surfaces have gained significant attention. Superhydrophobic surfaces demonstrate notable advantages in addressing interfacial issues, and superhydrophobic coatings exhibit excellent waterproofness, anti-fouling, self-cleaning, anti-corrosion, and additional capabilities, making them promising next-generation waterproof materials. However, the complex preparation process, coupled with poor wear resistance and environmental durability, severely limits their practical applications. Therefore, this article started from simplifying the preparation process and improving the durability of the coatings. Epoxy resin (E51) was used as the film-forming material, and carbon nanotubes (CNTs) and dual-sized SiC particles (nano-SiC and micro-SiC) were used as the fillers. Room temperature vulcanized silicone rubber (RTV) was used as a binder interacting with epoxy resin to promote the interface interaction between the fillers and the polymers. This process resulted in the successful preparation of superhydrophobic coatings with outstanding comprehensive performance. When the ratio of μ-SiC to n-SiC was 1:1, the prepared coating exhibited the best superhydrophobic properties with a water contact angle (WCA) of 167.4° and a sliding angle (SA) of 4.6°. Even after undergoing severe mechanical tests, such as sandpaper abrasion for 1000 cycles, sand impact for 100 cycles, cross-cut test, and tape-peeling for 70 cycles, the coatings still maintained their non-wetting Cassie-Baxter state. Furthermore, even after immersion in strong acid, strong alkali and 3.5 wt% NaCl solutions for 6 days, keeping at 500 °C for 2 hours, and exposure to ultraviolet for 6 days, the coatings still exhibited excellent superhydrophobicity. This suggested that the prepared coating had excellent chemical stability and high-temperature resistance. In addition, the superhydrophobic coating exhibited exceptional capabilities in self-cleaning, anti-corrosion, anti-icing, and de-icing properties. Furthermore, this coating, applicable to diverse substrates including board, steel, paper, and glass, demonstrated an impressive water contact angle (WCA) and sliding angle (SA). The spraying method offers the benefits of simplicity and cost-effectiveness. This is poised to significantly broaden its practical applications in various fields, including construction, transportation, and the chemical industry.

Robust Ni/WC superhydrophobic surfaces by electrodeposition

A rapid one-step electrodeposition method for fabrication of the superhydrophobic nickel/cobalt alloy surfaces with excellent robustness and durability features

Design and fabrication of a stable Ni-PTFE-SiC superhydrophobic anticorrosive coating by electrodeposition

Superhydrophobic Ni nanocone surface prepared by electrodeposition and its overall performance

Superhydrophobic and anticorrosion Ni-B/WC@MoS 2 composite coatings deposited via jet electrodeposition assisted with ultrasonics

Construction of superhydrophobic tungsten carbide via laser processing and its thermal, chemical and mechanical properties

Corrosion resistance of superhydrophobic Ni-B/TiC composite coatings prepared by electroless deposition

Fabrication of superhydrophobic self-cleaning Ni-Co-MoS 2 /Ni composite coating

Facile Fabrication of Durable Copper-Based Superhydrophobic Surfaces via Electrodeposition

A High-Efficiency Preparation Method of Super Wear-Resistant Superhydrophobic Surface with Hierarchical Structure Using Wire Electrical Discharge Machining

Designing a Robust Ni-P/CeO2 Superhydrophobic Composite Coating for Synergistically Enhanced Corrosion Protection and Friction Reduction Performance

Facile Preparation of Robust Superamphiphobic Surface by Electrochemical Etching Process Based on the SiC/Al Composites

Long-Term Durability of Robust Super-Hydrophobic Co–Ni-Based Coatings Produced by Electrochemical Deposition

Robust Superhydrophobic Surfaces via the Sand-In Method

Facile Design and Fabrication of Superwetting Surfaces with Excellent Wear-Resistance

Study on the Corrosion Resistance of Superhydrophobic Ni-Co- P-BN(h) Nanocomposite Coatings Prepared by Electrochemical Machining and Fluorosilane Modification

Achieving hierarchical structure with superhydrophobicity and enhanced anti-corrosion via electrochemical etching and chemical vapor deposition

Preparation of corrosion-resistant superhydrophobic Ni-Co coatings on copper mesh and oil-water separation properties

Fabrication of cerium myristate coating for a mechanochemically robust modifier-free superwettability system to enhance the corrosion resistance on 316L steel by one-step electrodeposition

Fabrication of high-durability superhydrophobic coatings based on dual-sized SiC particles

Fabrication of Superhydrophobic Coatings for Corrosion Protection by Electrodeposition: A Comprehensive Review