Abstract:Nanostructured and conventional alumina–3 wt.% titania monolithic coatings were deposited by air plasma spraying (APS). The thermal diffusivity was measured by the laser flash technique. The thermal diffusivity of the nanostructured Al2O3–3 wt.% TiO2 coating was higher compared with that of the corresponding conventional coating at temperature ranging from 200 to 1000 °C. For the nanostructured coating, there was no difference in the thermal diffusivity between during heating and cooling. However, the thermal diffusivities of the conventional coating were higher during cooling than those during heating. SEM and TEM examination showed that the nanostructured coating contained equiaxed grains with sizes from 150 to 800 nm besides splat lamellae. In the nanostructured coating, most of columnar grains in splat lamellae were less than 200 nm. Splat lamellae of the nanostructured coating bonded well each other and their thickness ranged from 0.4 to 1 μm. The decrease of thermal diffusivity of the nanostructured coating was attributed to the increase of grain boundaries and defective crystal structure. The stability of thermal diffusivity of the nanostructured coating was considered to relate to the absence of narrow long micro-cracks between splat lamellae. Nanostructured and conventional alumina–3 wt.% titania monolithic coatings were deposited by air plasma spraying (APS). The thermal diffusivity was measured by the laser flash technique. The thermal diffusivity of the nanostructured Al2O3–3 wt.% TiO2 coating was higher compared with that of the corresponding conventional coating at temperature ranging from 200 to 1000 °C. For the nanostructured coating, there was no difference in the thermal diffusivity between during heating and cooling. However, the thermal diffusivities of the conventional coating were higher during cooling than those during heating. SEM and TEM examination showed that the nanostructured coating contained equiaxed grains with sizes from 150 to 800 nm besides splat lamellae. In the nanostructured coating, most of columnar grains in splat lamellae were less than 200 nm. Splat lamellae of the nanostructured coating bonded well each other and their thickness ranged from 0.4 to 1 μm. The decrease of thermal diffusivity of the nanostructured coating was attributed to the increase of grain boundaries and defective crystal structure. The stability of thermal diffusivity of the nanostructured coating was considered to relate to the absence of narrow long micro-cracks between splat lamellae.

D. C. Plasma-Sprayed Coatings of Nanostructured Alumina-Titania-Silica

Microstructure of alumina–3wt.% titania coatings by plasma spraying with nanostructured powders

Characterization of Alumina–3 Wt.% Titania Coating Prepared by Plasma Spraying of Nanostructured Powders

Fabrication and Evaluation of Plasma Sprayed Nanostructured Alumina–titania Coatings with Superior Properties

Abrasive wear characteristics of plasma sprayed nanostructured alumina/titania coatings

Microstructure, formation mechanism and properties of plasma-sprayed Cr7C3—CrSi2—Al2O3 coatings

Toughening and Strengthening Mechanism of Plasma Sprayed Nanostructured Al2O3–13 Wt.%tio2 Coatings

The dependency of microstructure and properties of nanostructured coatings on plasma spray conditions

Influence of Composite Powders’ Microstructure on the Microstructure and Properties of Al2O3–TiO2 Coatings Fabricated by Plasma Spraying

Effects of Treatment Process and Nano-Additives on the Microstructure and Properties of Al2O3-TiO2 Nanocomposite Powders Used for Plasma Spraying

Structure and Properties of MoSi2-CoNiCrAlY Nano-composite Coating by Plasma Spraying

Microstructure and Wear Behaviors of Plasma-Sprayed MoAlB Ceramic Coating

Study on performance of nano-zirconia coating deposited by plasma spraying

Thermal diffusivity of plasma sprayed monolithic coating of alumina–3 wt.% titania produced with nanostructured powder

Nanostructured Yttria Stabilized Zirconia Coatings Deposited by Air Plasma Spraying

Preparation Nanostructured FeAl2O4-Al2O3-Fe Composite Coating by SHS Plasma Spraying Technology

The Influence of Powder Types and Plasma Spray Conditions on Abrasive Wear of Nanostructured and Conventional Al2o3/Tio2 Coatings

The influence of powder types and plasma spray conditions on abrasive wear of nanostructured and conventional Al2O3TiO2 coatings

Corrosion of Plasma Sprayed NiCrAl/Al2O3–13 Wt-%Tio2 Coatings with and Without Sealing

Microstructure and Electrochemical Properties of Molybdenum Base Amorphous and Nanocrystalline Alloy Coatings by Plasma Spraying

Al–Cu–Cr Quasicrystalline Coatings Prepared by Low Power Plasma Spraying