Abstract:The severe oxidation of metal elements leads to a large amount of oxide inclusions that hinder the formation of metallurgical bonds across intersplat interfaces during thermal spraying in an ambient atmosphere, which further degrades the performance of thermally sprayed metal coatings. Controlling the oxidation of metal elements during spray deposition remains a significant challenge. In this paper, the thermodynamic and kinetic requirements of in-situ in-flight deoxidation by adding deoxidizer elements (diamond particles) to Fe / Al spray powders to achieve oxide-free molten droplets in an ambient atmosphere were investigated. Fe / Al / 2.5C composite powders containing 2.5wt.% diamond particles were prepared by mechanical alloying. Atmospheric plasma spraying (APS) was used to generate an oxide-free molten spray of FeAl particles at temperatures higher than 2 000 degrees C. This was achieved by the in-situ self-oxide cleaning effect of in-flight particles by carbon, which prevented metal droplets from oxidizing in an open atmosphere. For comparison, a FeAl coating was also deposited using Fe / Al composite powders prepared by mechanical alloying. The particle velocity and temperature were measured by a commercial thermal-spraying particle diagnostic system. The microstructures of the coatings were characterized by scanning electron microscopy and X-ray diffraction. The chemical compositions of the coatings were measured by inductively coupled plasma spectroscopy. The adhesive strength and hardness of the plasma-sprayed FeAl-based coatings were tested. The results show that under the combined effects of plasma- jet heating and the FeAl exothermic reaction, the heated FeAl spray particles could reach a high temperature of over 2 100 degrees C, which meets the thermodynamic conditions for carbon in-situ deoxidation. Because oxidation occurs from the surface of an in-flight molten droplet, to maintain continuous deoxidation of the molten FeAl droplet, the rapid transfer of carbon from the interior of the molten droplet to the surface is necessary. It was confirmed that the strong convection flow of the molten metal droplets satisfied the kinetic conditions of carbon in-situ in-flight deoxidation. The oxygen content in the APS-sprayed FeAl coatings increased with the increase of the spray distance. In contrast, the oxygen content in the APS-sprayed FeAl / 2.5C coatings decreased from 1.01 wt.% to 0.48 wt.% as the spray distance increased from 70 mm to 150 mm. This was accompanied by the decrease in carbon content from 1.41 wt.% to 0.31 wt.%, indicating the effective protection of Fe and Al from oxidation by the carbon in the droplet. Compared with the oxygen content of 3.67 wt.% in traditional FeAl coating, the oxygen content of the FeAl / 2.5C coatings was reduced to less than 0.5 wt.%. Considering that the carbon content of the coatings decreased as the spray distance increased, the results confirm that the in-flight oxidation of Fe and Al was suppressed by the preferential sacrificial oxidation of carbon in the molten droplets. Thus, the oxide in the FeAl / 2.5C coatings was mainly attributed to post-deposition oxidation. Moreover, the FeAl droplet reached the temperature to realize the spread-fusing self-metallurgical bonding effect for FeAl splats. The coatings exhibited a dense microstructure with an apparent porosity of less than 0.5%. The adhesive bonding strength of the prepared coatings exceeded 59.2 MPa owing to metallurgical bonding. The hardness of the coatings reached 590 HV0. 3, which was approximately twice that of traditional FeAl coatings. This was attributed to the reinforcement provided by the Fe3AlCx cementite phase resulting from the residual carbon in the coating.

Structure and performance of γ-alumina washcoat deposited by plasma spraying

Influence of an aluminized intermediate layer on the adhesion of a γ-Al2O3 washcoat on FeCrAl

Microstructure, formation mechanism and properties of plasma-sprayed Cr7C3—CrSi2—Al2O3 coatings

Effects of plasma-sprayed NiCrAl/ZrO2 intermediate on the combination ability of coatings

D. C. Plasma-Sprayed Coatings of Nanostructured Alumina-Titania-Silica

Preparation and characterization of supersonic plasma sprayed Al–Al2O3–Cr2O3 composite coatings on magnesium alloy substrate

Influence of Plasma-Sprayed NiCrAl/ZrO_2 Intermediate on Adhesion of FeCrAl/γ-Al_2O_3

Friction and wear characteristics of in-situ Cr+(Cr,Al)2O3 composite coating fabricated by plasma spraying

Microstructure and Properties of Al2O3-13wt.%TiO2-Reinforced CoCrFeMnNi High-Entropy Alloy Composite Coatings Prepared by Plasma Spraying

Improve the tribological performance of anodic coating by plasma discharge treatment

Mechanism of Suppressing Oxidation of FeAl Molten Droplet by Adding C to Powder and Its Effect on Microstructure and Properties of Plasma-sprayed Coating

Microstructure and Wear Behaviors of Plasma-Sprayed MoAlB Ceramic Coating

Plasma Spraying NiCoCrAlY-Cr2O3-AgMo Coatings: Fabrication and Tribological Mechanisms

Study of the Mechanical Properties and Thermal Control Performance of Plasma-Sprayed Alumina Coating on Aluminum Alloy Surface

High-loading washcoat of γ-alumina on FeCrAlloy mesh with acid-free slurry

Development mechanism and performance of Al2O3-PF composite coating on epoxy resin matrix composite surface by supersonic plasma spraying

Microstructure, adhesion, microhardness, abrasive wear resistance and electrical resistivity of the plasma sprayed alumina and alumina–titania coatings

Microstructure and properties of Al2O3–ZrO2–TiO2 composite coatings prepared by plasma spraying

Study on Properties of Pure Al Coatings and Al/SiC Composite Coatings by Plasma Transferred Wire Spraying

Properties of alumina coatings prepared on silica-based ceramic substrate by plasma spraying and sol-gel dipping methods

Fundamental understanding on the microstructure and corrosion resistance of Cr-(Cr, Al)2O3 composite coatings in-situ synthetized by reactive plasma spraying