Effects of Ni-5 wt% Al/Bi2O3 addition and heat treatment on mechanical and tribological properties of atmospheric plasma sprayed Al2O3 coating
Huwei Sun,Gewen Yi,Shanhong Wan,Juanjuan Chen,Benbin Xin,Wenzhen Wang,Yu Shan,Yina Wen
DOI: https://doi.org/10.1016/j.surfcoat.2023.129935
IF: 4.865
2023-11-01
Surface and Coatings Technology
Abstract:To solve the problem of high friction and wear of the plasma sprayed Al2O3 coating in a wide temperature range, two Al2O3-based composite coatings, namely Al2O3-(NiAl-Bi2O3) coating and Al2O3-(NiAl-Bi2O3)-H coating (heat treatment), were prepared by involving Ni-5 wt% Al and Bi2O3, and applying a simple heat treatment. Compared to the Al2O3 coating, two Al2O3-based composite coatings attained increased toughness and adhesive strength. In particular, heat treatment endowed Al2O3-(NiAl-Bi2O3)-H coating with improved compositional homogeneity and more NiBi intermetallic compound and α-Al2O3 phases. In terms of tribological behavior, when subjected to rubbing against the counterpart Al2O3 ball, Bi2O3 and NiBi were shown to have good lubricating properties, and they exerted friction-reducing and anti-wear effects in both Al2O3-based composite coatings at 25 and 400 °C, respectively. At 800 °C, under the action of thermo-mechanical coupling, a tribo-oxide layer composed of multiple oxides (Al2O3, Bi2O3, NiO and Bi2Al4O9) was generated on the worn surface of the two composite coatings, achieving the excellent lubrication and wear-resistance.
physics, applied,materials science, coatings & films