Preparation, structure and mechanical properties of Sialon ceramics by transition metal-catalyzed nitriding reaction
Qing-Ming Xiong,Zhi Chen,Jun-Tong Huang,Meng Zhang,Hui Song,Xi-Feng Hou,Xi-Bao Li,Zhi-Jun Feng
DOI: https://doi.org/10.1007/s12598-020-01385-6
IF: 6.318
2020-03-20
Rare Metals
Abstract:<span class="a-plus-plus abstract-section id-a-sec1 outputmedium-all"><p class="a-plus-plus">Sialon ceramics were prepared by the nitridation of Si, Al and Al<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">3</sub> powders with the transition metals (Fe, Co, Ni) catalysts. The phase composition, microstructure and mechanical properties of specimens were studied. Compared with the catalyst-free specimen, the addition of Fe, Co and Ni greatly promoted the nitridation process of Sialon ceramics and improved the weight gain rate and mechanical properties of specimens. With the increased content of catalysts, the apparent porosity of the products decreased first and then increased, contrary to flexural strength and compressive strength. The specimen with 2.5 wt% Fe had the highest flexural strength 145.8 MPa, and it exhibited the highest compressive strength of 594.6 MPa when Co content was 2.5 wt%, whereas they were 71.9 and 78.7 MPa, respectively, when without catalyst.</p></span><span class="a-plus-plus abstract-section id-a-sec2 outputmedium-online"><h3 class="a-plus-plus">Graphic abstract</h3></span>
materials science, multidisciplinary,metallurgy & metallurgical engineering