MICROSTRUCTURE CONTROL AND MECHANICAL PROPERTIES OPTIMIZATION OF Α-Sialon CERAMICS

ZHOU Yu,YE Feng,LIU Limeng
DOI: https://doi.org/10.3321/j.issn:0454-5648.2007.08.014
2007-01-01
Abstract:The effects of rare-earth additives (yttrium, ytterbium, and/or neodymium), sintering processes, and post heat-treatment on the microstructure and mechanical properties of α-sialon ceramics were studied. The results reveal that control of the kinetics for α-sialon formation is essential for the growth of self-toughening elongated grains. The effects of the sintering process and post heat-treatment on the development of elongated α-sialon grains are dependent on its composition and the type of additive rare earth cations. No α phase to β-sialon phase transformation was observed in the investigated Y-α-sialon after annealing in the temperature range from 1 300 ℃ to 1 700 ℃, whereas annealing at 1 500 ℃ changed the morphology of the elongated α-sialon grains to equiaxed, thus decreasing its toughness.