Abstract:The behavior of SiO2 in the precipitation of Gibbsite in caustic aluminate solution has been investigated by ion membrane electrolysis.The microstructure of unseeded precipitation of aluminum hydroxide and its surface elements were characterized by using scanning electronic microscope(SEM) and Electron Spectrometer.The results show that silicon dioxide influenced on precipitated process obviously.The concentration change of SiO2 upon 0.60 g/L in the precipitation process was thought to be undertaken there-step: decrease quickly at first,a lag period step secondly and a slow step thirdly.The precipitation ratio are up to 50% after six hours in pure solution or sodium aluminate solution with SiO2.The precipitation rate was faster at 70℃ comparing with 60℃,especially at the first hour its precipitation ration almost 40%,which indicates that the decomposition of supersaturated sodium aluminate solution is controlled by chemical reaction.The number of particle size under 10 μm was increased in the present of SiO2,and the effecting of SiO2 on the number of fine particle size at 60℃ was more than at 70℃.The SEM present that the surface of Al(OH)3 from unseeded precipitated pure solution were lubricity,but there were some fine particle size in the surface of Al(OH)3 from solutions with SiO2,especially some foreign colloid-like crystal was appeared.In colloid area,four elements (Si,Al,O and Na) was detected by Electron Spectrometer,it is speculated that sodium aluminum silicate may be exist.

Impurity Na2O in Carbonization Precipitation from Sodium Aluminate Solution with High Al2O3 Concentration

Control of Na2O Content in Aluminum Hydroxide from Carbonization of Sodium Aluminate Solution with High Alumina Concentration

The Feasible Research on Carbonization Precipitation with High Alumia concentration in Sodium Aluminate Solution

An Experimental Study of Extracting Aluminum Hydroxide from High Caustic Sodium Aluminate Solution

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Thermodynamics of Carbonization of Aluminate Solution

Effect of silicon-containing impurity on precipitation of sodium aluminate solution and interaction mechanism

Behavior of SiO2 in the Precipitation of Caustic Aluminate Solutions

Influence of Inorganic Salt Impurities on Seed Decomposition Rate in Sodium Aluminate Solutions

Kinetics of Carbonation Decomposition of Sodium Aluminate Solution

Effect of Na2o on Dissolution Rate of Alumina in Cao-Al2o3-Mgo-Sio2 Slag

Variation of Soda Content in Fine Alumina Trihydrate by Seeded Precipitation

Reaction Behavior of Silica in Sodium Aluminate Solution

Removal of sodium humate from sodium aluminate solution by adsorption with alumina dust

Decomposition of supersaturated sodium aluminate solution

Effects of Caustic Sodium Concentration and Molecular Ratio of Na2o to Al2o3 on Agglomeration in the Precipitation Process

Anti-causticization of Calcium Carbonate in Sodium Aluminate Solution

Increasing Precipitation Rate from Sodium Aluminate Solution by Adding Active Seed and Ammonia

Removal of S2− ion from sodium aluminate solutions with sodium ferrite

Influence of Sodium Phosphate Impurity on the Seeded Precipitation of Sodium Aluminate Solution

Alumina Recovery from Sodium Hydrate Alumino-Silicate