Effect of Iron Oxide Nanoparticles on Thermal Stability of Aluminium Titanate Ceramics

Zhihua SUN,Kaiping LIU,Minqiang WANG,Minwu LIU

DOI: https://doi.org/10.7521/j.issn.0454-5648.2013.04.03

2013-01-01

Abstract:The aluminum titanate solid solution[Al2(1-x)Fe2xTiO5] was prepared using synthesized precursors of aluminum titanate (Al2TiO5) and synthesized iron oxide (Fe2O3) nanoparticles by solid state reaction as starting materials, firing at different temperatures for 2 h. The effect of Fe2O3 nanoparticles content and fired temperature on thermal stability of aluminium titanate ceramics was investigated by X-ray diffraction, electron probe micro-analyzer and calculation of their lattice constant and thermal decomposition. The results showed that 1) Fe2O3 nanoparticles was reacted with Al2TiO5 easily, thermal decomposition of aluminium titanate ceramics can be reduced by doping Fe2O3 nanoparticles with the formation of solid solution; 2) The lattice constant of Al2(1-x)Fe2xTiO5 increased and thermal decomposition decreased gradually as the Fe2O3 nanoparticles content increasing, but the lattice constants of Al2(1-x)Fe2xTiO5 remained unchanged or decreased and thermal decomposition increased as the Fe2O3 nanoparticles content exceed 10%; 3) The fired temperature of lattice ceramics affects its thermal decomposition greatly in improving thermal stability by doping Fe2O3 nanoparticles, thermal decomposition decreased gradually with a rise temperature, whereas thermal decomposition had no significant change when the fired temperature exceeds 1 350°C.