Abstract:The work aims to study frication property and wear mechanism of Cr7C3 coating or GCr15 substrate being rubbed with 9310 alloy steel for sprag overrunning clutch. Cr7C3 coating sample was prepared on GCr15 substrate by adopting chemical 表面摩擦磨损与润滑第 47 卷第 8 期雷美娟等:斜撑式超越离合器用 Cr7C3 涂层和 GCr15 基体的磨损行为研究 ·91· vapor deposition technology. The thickness and phase composition of Cr7C3 coating and microhardness of both samples (with and without Cr7C3 coating) were analyzed by scanning electron microscope (SEM) (with EDS analysis),X-ray diffractometer (XRD) and nano-indenter. Friction and wear properties of Cr7C3 coating and GCr15 substrate were investigated with ball-on-disk SRV-4 high temperature tribotester. Wear scar conditions of the materials were characterized systematically with 3D white light interferometer surface profiler and SEM. It was calculated that the thickness of Cr7C3 coating was about 4~6 μm. And it was mainly composed of phase Cr7C3 and phase (Cr,Fe)7C3. Average surface microhardness of the Cr7C3 coating was 22.709 GPa, nearly twice that of GCr15 substrate (11.198 GPa). Under experimental parameters, frication coefficient of the Cr7C3 coating ranged between 0.18~0.24 while that of GCr15 substrate ranged between 0.15~0.20. Wear rate of GCr15 was about 4~6 times that of Cr7C3 coating at the sliding speed of 60 mm/s and normal load of 20~60 N, but 7~11 times that of Cr7C3 coating at the sliding speed of 100 mm/s. The wear mechanism of GCr15 substrate was typical furrow wear, and that of Cr7C3 coating was mainly furrow wear and fatigue wear at the sliding speed of 100 mm/s and normal load of 60 N. Cr7C3 coating has high microhardness and excellent wear resistance, which can contribute to better wear resistance of the substrate and higher usability of sprag overrunning clutch.

Wear of GCr15 Steel in Coupling of Rolling and Sliding

Sliding Friction and Wear Properties of GCr15 Steel under Different Lubrication Conditions

Wear Behaviour and Microstructural Changes of SiCw-Al Composite under Unlubricated Sliding Friction

Friction and wear behavior of Fe2AlB2 nanolaminates against GCr15 steel counterpart

Study on Fretting Wear Properties of GCr15 Steel Via Ultrasonic Surface Rolling Process

Investigation on Rolling Contact Fatigue of 55 Medium-Carbon Steel

Influence mechanism of grinding surface quality of 20CrMnTi steel on contact failure

Wear Behavior of WC/GCr15 Steel Composite Prepared by Electroslag Melting and Casting

Wear Rate, Frictional Temperature, and Energy Consumption of Steel 52100 with Different Microstructures During Sliding

Anomalous ligand binding by a class of high spin c-type cytochromes.

Sliding abrasive wear characteristics of steels with different hardness

Insights into the microstructure characteristics, mechanical properties and tribological behaviour of gas-phase chromized coating on GCr15 bearing steel

Microstructure Evolution of a Hypereutectoid Pearlite Steel under Rolling-Sliding Contact Loading

Correlating numerical modelling with experimental studies to quantify the wear resistance of high-carbon chromium bearing steel in mixed lubrication

Friction And Wear Characteristics Of M2 High Speed Steel At High Speed Dry Sliding Condition

Tribological Behavior and Wear Mechanism of Cu-SiO2 Sintered Composite under Different Sliding Speeds

Study on fretting friction properties based on GCr15 alloy and liquid epoxy resin protective coatings on GCr15 alloy

Friction and wear characteristics of plasma-sprayed WC coatings in dliding against GCr15 steel

Wear Behavior of Cr7C3 Coating and GCr15 Substrate for Sprag Overrunning Clutch

Ex-situ additively manufactured FeCrMoCB/Cu bulk metallic glass composite with well wear resistance

Wear Property and Wear Mechanisms of High-Manganese Austenitic Hadfield Steel in Dry Reciprocal Sliding