Abstract:<p>For wear resistant steels, there is generally a linear relationship between the initial hardness and wear resistance, yet a high initial hardness limits the formability of components. The intrinsic ductility of austenite and strain hardening produced from the transformation-induced plasticity (TRIP) effect during service opens a new window for this contradiction. Herein, the wear resistance and the corresponding failure mechanisms of 5Mn steels after different heat treatment processes were evaluated using a ball-on-disk sliding test under dry conditions. The wear behaviors of the counterbodies were also studied to elucidate the wear mechanism of the tribo-system. The results show that the microstructures of the hot-rolled and air-cooled steel mainly comprised martensite. When the intercritical annealing temperature was relatively low (<695°C), the microstructure primarily consisted of reversed austenite and ferrite. The samples annealed at 630°C, 645°C, 660°C, and 675°C had a similar initial hardness, while the sample annealed at 675°C possessed a wear resistance that was 3.25 times that of the steel annealed at 630°C. The large difference in the wear resistance was predominately due to the gradient of strain hardening provided by the varied amount and mechanical stability of the retained austenite. The transformation from austenite to martensite, which has an increased hardness, improves the work hardening. A strengthening layer formed with a certain thickness that provided stress support during the wear process and enhanced the wear resistance. When the annealing temperature reached 695°C, a large amount of secondary martensite was generated from austenite that had a low thermal stability, which improved the initial hardness and wear resistance. The steels with a large amount of martensite had an enhanced wear resistance, but the elongation severely deteriorated, leading to unsatisfactory formability. The present work provides guidance for designing novel steels with an excellent balance of good formability and decent wear resistance by precisely adjusting the characteristics of the retained austenite.</p>

Sliding abrasive wear characteristics of steels with different hardness

Wear Behaviour and Microstructural Changes of SiCw-Al Composite under Unlubricated Sliding Friction

The Effects of Ageing and Whisker-Orientation on Wear Behaviour of SiCwAl Composites under Unlubricated Sliding Friction

The effect of hardness on the transition of the abrasive wear mechanism of steels

A study of the abrasive wear of carbon steels

Dependence of Wear Behaviors of Hardmetal Yg8b on Coarse Abrasive Types and Their Slurry Concentrations

Wear behavior and damage characterization for AISI 52100 bearing steels: Effect of hardness and spherical carbides

New insight into the dry rolling-sliding wear mechanism of carbide-free bainitic and pearlitic steel

Wear Property and Wear Mechanisms of High-Manganese Austenitic Hadfield Steel in Dry Reciprocal Sliding

Effect of different hardness units on fatigue wear resistence of low hardenability steel

Sliding wear resistance of Fe–30Mn–8Al–1.2C steel modulated by κ–carbide

Abrasive Wear Mechanisms of S235JR, S355J2, C45, AISI 304, and Hardox 500 Steels Tested Using Garnet, Corundum and Carborundum Abrasives

High-stress abrasive wear characteristics of ultra-high strength press-hardening steel

Sliding wear of medium-carbon bainitic/martensitic/austenitic steel treated by short-term low-temperature austempering

Surface self-nanocrystallization and -lubricating dependent wear resistance of austenitic steels at same initial hardness level

Unraveling the significant role of retained austenite on the dry sliding wear behavior of medium manganese steel

Sliding Friction and Wear Properties of GCr15 Steel under Different Lubrication Conditions

Investigation on the parameters optimization and sliding wear behaviors under starved lubrication of discrete laser surface hardened 25CrNi2MoV steel

Friction and wear characteristics of plasma-sprayed WC coatings in dliding against GCr15 steel

Effect of hardenability on microstructure and property of low alloy abrasion-resistant steel

Three-body abrasion wear resistance of TiC-reinforced low-alloy abrasion-resistant martensitic steel under dry and wet sand conditions