Abstract:To reveal the influence mechanism of the grinding surface quality of 20CrMnTi steel components on the tribological characteristics and contact fatigue performance, accelerated tests for sliding friction wear and fatigue damage were carried out. Tribological characteristics and contact fatigue performance get worse with increasing surface roughness while getting better with increasing surface microhardness. Residual compressive stress is conducive to inhibiting the initiation and propagation of cracks and promoting contact fatigue performance. Additionally, mechanical friction, abrasive wear, adhesive wear and fatigue damage coexist and form a competing failure mechanism under the synergistic effect of frictional wear and contact fatigue failure. The damage process mainly manifests as wear, stress concentration induced fatigue, microcracks, pitting, and spalling in the shallow layer. This study is more beneficial to promote the 20CrMnTi steel transmission parts manufacturing products for high precision, low damage, and long life.
What problem does this paper attempt to address?
### Problems the paper attempts to solve
This paper aims to reveal the influence mechanism of the grinding surface quality of 20CrMnTi steel on its tribological characteristics and contact fatigue performance. Specifically, the main research problems include:
1. **Influence of surface roughness on tribological characteristics**:
- How does surface roughness affect the friction coefficient and wear behavior?
- The wear mechanism of rough surfaces under dry sliding friction and lubricated conditions.
2. **Influence of surface micro - hardness on tribological characteristics**:
- How does surface micro - hardness affect the friction coefficient and wear behavior?
- Can improving surface micro - hardness improve tribological performance?
3. **Influence of residual compressive stress on contact fatigue performance**:
- How does residual compressive stress inhibit the initiation and propagation of cracks, thereby improving contact fatigue performance?
- The influence of the residual compressive stress introduced by shot peening treatment on the contact fatigue life.
4. **Relationship between surface integrity and contact fatigue damage**:
- Explore the synergy between mechanical friction, abrasive wear, adhesive wear and fatigue damage.
- Analyze the influence mechanism of surface integrity (such as roughness, micro - hardness, residual stress) on contact fatigue damage.
5. **Optimize the manufacturing process to improve component performance**:
- How to improve the precision of 20CrMnTi steel transmission parts, reduce the risk of damage and extend the service life by controlling the surface quality?
### Experimental methods and result analysis
In order to explore the above problems, the researchers carried out the following experiments:
- **Reciprocating sliding friction and wear tests**: Using the MFT - R4000 tester, friction and wear tests were carried out under different conditions (such as load, frequency, lubrication state, etc.), and the influence of surface roughness and micro - hardness on tribological characteristics was analyzed.
- **Rolling contact fatigue tests**: Using the YS - 2 ball - disk contact fatigue tester, the fatigue damage of the surface was evaluated under continuous stress, and the influence of surface integrity on contact fatigue performance was studied.
Through these experiments, the researchers found that:
- **The greater the surface roughness, the higher the friction coefficient**, and the more serious the wear, especially under dry sliding friction conditions. Rough surfaces are prone to stress concentration, leading to the initiation of near - surface contact fatigue cracks.
- **Improving surface micro - hardness can reduce the friction coefficient**, improve tribological performance, reduce adhesive wear, and thus improve the wear resistance of the material.
- **Residual compressive stress helps to inhibit the initiation and propagation of cracks**, significantly improving the contact fatigue life. Shot peening treatment can introduce large residual compressive stress on the surface, effectively improving the contact fatigue performance.
In general, this research provides important experimental and theoretical basis for optimizing the manufacturing process of 20CrMnTi steel transmission parts, which is helpful for improving the precision of parts, reducing noise and extending the service life.