Abstract:To study the effect of the surface properties on the bending fatigue performance of heavy-duty gear steel, the authors of this paper used the ultrasonic surface rolling process (USRP) to strengthen 20Cr2Ni4A carburized gear steel. USRP is a novel technique in which the ultrasonic technology is incorporated into the concept of conventional deep rolling. In this study, we illustrated how the surface properties and cross-section mechanical property influence the three-point bending fatigue life of the samples before and after USRP treatment. At the same time, the predicted failure probability-stress-number of cycles (P-S-N) curve was drawn, and the fatigue fracture was analysed. The results show that the fatigue limit increased from 651.36 MPa to 918.88 MPa after USRP treatment. The fatigue source is mainly from the sample interior or surface scratches, and the fatigue performance is positively correlated with the results of the material surface roughness, surface residual stress and surface hardness. At the same time, combined with the change in the phase structure, dislocation structure, residual stress and hardness of the cross section of the material, it is found that the USRP process turns the steel into a gradient material with five layers. Finally, the coupling mechanism between the ultrasonic surface strengthening deformation layer and the carburized layer of 20Cr2Ni4A carburized gear steel is presented, and the grain structure distribution diagram of the section of the 20Cr2Ni4A model after surface strengthening treatment was simulated. The mechanism that influenced the fatigue performance after USRP treatment is explained from the perspectives of the surface and cross section of the samples.

Experimental Study on the Influence of Surface Carbon Content on Crack Initiation for 20Cr2Ni4A Steel

X-ray diffraction comparison studies between the laser hardened gear and carburized gear

Experimental Study on Vacuum Carburizing Process for Low-Carbon Alloy Steel

Bending Fatigue Behaviour and Fatigue Endurance Limit Prediction of 20Cr2Ni4A Gear Steel after the Ultrasonic Surface Rolling Process

Influence mechanism of grinding surface quality of 20CrMnTi steel on contact failure

Effect of Carbides on Thermos-Plastic and Crack Initiation and Expansion of High-Carbon Chromium-Bearing Steel Castings

Rolling Contact Fatigue Failure Mechanism of Martensitic Bearing Steel after Carbonitriding

Study on Cracks and Process Improvement for Case Hardened Gear Shaft Straightening

Microstructure Evolution and Mechanical Properties of High-Temperature Carburized 18Cr2Ni4WA Steel

Surface strengthening mechanism of the active grinding carburization

Surface Morphology and Subsurface Microstructure Evolution when Form Grinding 20cr2ni4a Alloys.

Vertical Short Crack Initiation in Medium Carbon Bainitic Steel Under Mild Tractive Rolling Contact

Improving the Wear Resistance of Heavy-Duty Gear Steels by Cyclic Carburizing

Fatigue Crack Initiation and Propagation at High Temperature of New-Generation Bearing Steel

Mechanical Properties and Formation Mechanism of Surface Hard Nanocrystalline Carbon Diffusion Layer on 18Cr2Ni4WA Steel Induced by Supersonic Fine Particle Bombarding

Rolling Contact Fatigue Crack Initiation in Medium Carbon Bainitic Steel

Effect of Post-Plasma Nitrocarburized Treatment on Mechanical Properties of Carburized and Quenched 18Cr2Ni4WA Steel

Experimental Investigation on Microstructure Alteration and Surface Morphology While Grinding 20cr2ni4a Gears with Different Grinding Allowance Allocation

Effect of Ultrasonic Surface Rolling on the Microstructure and Corrosion Properties of Gear Steel 20CrNiMo After Carburizing

Predictions and Experiments on the Distortion of the 20Cr2Ni4A C-ring during Carburizing and Quenching Process

Influence of carbon layer hardness characteristics on RCF performance of carburized bearing steel and optimization of heat treatment process