Influence of (mg1/3nb2/3) Complex Substitutions on Crystal Structures and Microwave Dielectric Properties of Li2TiO3 Ceramics with Extreme Low Loss

Huan-Huan Guo,Di Zhou,Li-Xia Pang,Jin-Zhan Su

DOI: https://doi.org/10.1016/j.jmat.2018.09.002

IF: 8.589

2018-01-01

Journal of Materiomics

Abstract:A systematic investigation of the Li2Ti1-x(Mg1/3Nb2/3)(x)O-3 (0.1 <= x <= 0.35) solid solutions synthesized by traditional solid-state reaction method is reported in this work. In the composition range of 0.1 <= x <= 0.25, a monoclinic rock salt structured solid solution was formed. When x increased to 0.3, a phase transition from monoclinic to cubic phase, along with an order-disorder phase transition, was observed. With x increased from 0.1 to 0.35, the microwave permittivity (epsilon(r)) and temperature coefficient of resonant frequency (TCF) of the Li2Ti1-x(Mg1/3Nb2/3)(x)O-3 ceramics decreased linearly from 21.0 to 18.6, +27.1 to -19.4 ppm/degrees C, respectively. The Li2Ti0.75(Mg1/3Nb2/3)(0.25)O-3 ceramic sintered at 1170 degrees C shows high performance of microwave dielectric properties with a epsilon(r) similar to 19.6, a Qf (Q = quality factor = 1/dielectric loss; f = resonant frequency) similar to 109,770 GHz (at 7.7 GHz) and a near zero TCF similar to + 1.2 ppm/oC. Moreover, the burying sintering process can reduce the volatilization of lithium so that the porosity of Li2Ti0.75(Mg1/3Nb2/3)(0.25)O-3 ceramic was reduced effectively, which made Li2Ti0.75(Mg1/3Nb2/3)(0.25)O-3 ceramic promising for future applications. Selected area electron diffraction patterns, high-resolution transmission electron microscopy, Raman and far-infrared spectra were employed to study the relation between crystal structure and microwave dielectric properties in detail. (C) 2018 The Chinese Ceramic Society. Production and hosting by Elsevier B.V.