Structural Evolution And Microwave Dielectric Properties Of A Novel Li3mg2-X/3nb1-2x/3tixo6 System With A Rock Salt Structure

Xing Zhang,Bin Tang,Fang Zixuan,Hongyu Yang,Zhe Xiong,Lanxin Xue,Shuren Zhang

DOI: https://doi.org/10.1039/c8qi00956b

IF: 7.779

2018-01-01

Inorganic Chemistry Frontiers

Abstract:In this study, the Li3Mg2-x/3Nb1-2x/3TixO6 (0 x 0.6) solid solution was designed and synthesized by the solid-state reaction method. The ordering degree decreased with the increasing Ti content, and the ordered orthorhombic superstructure was continuously transformed to the disordered MgO-like cubic subcell structure with no other impure phase observed in the range of 0.12 x 0.38. During the phase transition process, the ordered domains were found in orthorhombic superstructures by TEM images. According to the variation of Raman patterns, the B-1g, B-2g and B-3g vibration modes which derive from Nb-Nb repulsive force in 8a sites were assigned to the band at 480 cm(-1). The relative densities and dielectric constants showed a similar nonlinear variation with the increase of Ti content. However, as x increased from 0 to 0.4, the phase transition contributed to the huge improvement of Q x f values from 82338 GHz to 125357 GHz (about 50%), but it also led to a slight decrease in the temperature coefficient of resonant frequency ((f)). After being sintered at 1260 degrees C for 6 h, the Li3Mg1.87Nb0.73Ti0.40O6 (x = 0.4) ceramics showed excellent microwave properties: epsilon(r) = 15.09, Q x f = 125357 GHz and (f) = -31.7 ppm degrees C-1.