A New Series of Low-Loss Multicomponent Oxide Microwave Dielectrics with a Rock Salt Structure: Li5MgABO8 (A = Ti, Sn; B = Nb, Ta)

Xing Zhang,Zhouhang Jiang,Bin Tang,Zixuan Fang,Zhe Xiong,Hao Li,Changlai Yuan,Shuren Zhang

DOI: https://doi.org/10.1016/j.ceramint.2020.01.029

IF: 5.532

2020-01-01

Ceramics International

Abstract:In this study, a series of Li(5)MgABO(8) (A =Ti, Sn; B = Nb, Ta) compounds were designed and synthesized through a solid-state reaction method. The XRD patterns showed that a single phase was formed for all the samples. All the peaks were indexed based on the MgO-Like rock salt cubic structure with space group Fm-3m (225) and the peaks indicated that crystals presented different (111) orientation growths in the prepared samples. For all the specimens, the relative density values of 94% and above could be achieved when the sintering temperature exceeded 1300 degrees C. The epsilon(r) values of the specimens showed an increasing trend when the sintering temperatures increased. However, the Q x f values firstly increased and then decreased with the rising temperatures. The electronically-induced strains and lattice-induced strains, which were evaluated by the bond strain index (BSI) and global instability index (GII), presented same variation trends as the Q x f values when the sintering temperature increased. The lowest dielectric loss was achieved in Li5MgTiNbO8 ceramics: epsilon(r) =17.55, Q x f = 109,700 GHz (f=7.379 GHz), tau(f) = -32.5 ppm/degrees C, when sintered at 1290 degrees C for 4 h.