Sintering Behavior, Structural Evolution, and Dielectric Properties of Li2+xMgTiO4Fx Microwave Dielectric Ceramics

Kui Liu,Dainan Zhang,Yuran Yang,Qisheng Yin,Yida Lei,Cheng Liu,Jie Li,Lichuan Jin,Yulong Liao,Huaiwu Zhang

DOI: https://doi.org/10.1016/j.jeurceramsoc.2023.06.032

IF: 5.7

2023-01-01

Journal of the European Ceramic Society

Abstract:Herein, the sintering behavior, structural evolution, microstructure, and dielectric properties of Li2+xMgTiO4Fx (0 <= x <= 5) ceramics were investigated. At x <= 0.75, Li2+xMgTiO4Fx ceramics formed a continuous solid solution with a cubic rock salt structure. Subsequently, a composite ceramic of Li2+xMgTiO4Fx and LiF was formed. It was found that the maximum mass percentage of LiF required to fully form a solid solution was between 11% and 13%. The Li2.75MgTiO4F0.75 exhibited the best dielectric properties: epsilon r = 16.52, Q x f = 123,574 GHz, and iota f =-18.11 ppm/degrees C. The substitution of F- for O2-resulted in a lower sintering temperature of 875 degrees C, which slightly suppressed the volatilization of Li, and thus optimized the dielectric properties. The decrease in lattice vibration damping behavior and the increase in electron cloud density resulted in lower dielectric losses. The reduction in molecular polarization rate led to a reduction in epsilon r, and the increase in bond energy optimized iota f. Good chemical compatibility with Ag electrode was demonstrated, indicating that Li2+xMgTiO4Fx ceramics have unlimited potential for LTCC applications.