Effects of Lattice Evolution and Ordering on the Microwave Dielectric Properties of Tin-Modified Li3Mg2NbO6-Based Ceramics

Xing Zhang,Xiao Zhang,Zixuan Fang,Zhe Xiong,Hongyu Yang,Shuren Zhang,Bin Tang

DOI: https://doi.org/10.1021/acs.jpcc.0c04762

2020-01-01

Abstract:In this contribution, the evolution of the crystal structure and the consequent effects on the microwave dielectric responses of the Sn4+-substituted Li3Mg2-x/3SnxNb1-2x/3O6 (0 <= x <= 1.5) ceramics were investigated as a function of the doping content. Interestingly, a wide range of solid solution (0 <= x <= 1.1) was obtained by the complex substitutions of Sn ions, and a composition-driven phase transition from the orthorhombic to cubic phase accompanied by an order-disorder transformation occurring in the range of 0.1 <= x <= 0.7. During the process of the phase transition, high-resolution transmission electron microscopy images showed the presence of a coherent phase boundary between the orthorhombic and cubic phases, which was formed owing to their similar rock-salt crystal configurations and small mismatches in the subcell-lattice parameters. Besides, the electron diffraction patterns indicated that the specimen with relatively low Sn concentration (x = 0.2) contained reconstructed superlattices. The unique layered structure of the end-member Li3Mg2NbO6 constrained the form of the substitution for the dopant ions, where the nonequivalent ions (Sn4+) were expected to enter into the Nb-Mg-Nb clusters in the Nb-rich layers preferentially, which was likely to be the cause of the formation of the reconstructed superlattices. The substitution-induced superlattices were highly related to the low dielectric loss of the specimens, and a small amount of Sn doping (0 <= x <= 0.3 mol) also lowered the internal strain of the samples. As the Sn concentration increased from 0 to 0.3, the quality factors (Q x f) were significantly enhanced from 91,700 to 118,700 GHz with the emergence of the reconstructed superlattices and the lowered internal strain.