Sintering Behavior, Microstructure and Microwave Dielectric Properties of Novel Temperature Stable Li3Mg2NbO6–tio2 Composite Ceramics

Wang Gang,Zhang Dainan,Zhang Huaiwu
DOI: https://doi.org/10.1557/adv.2019.2
2019-01-01
MRS Advances
Abstract:A novel series of temperature stable Li 3 Mg 2 NbO 6 –xTiO 2 ceramics were prepared by the conventional solid-state route. The effects of TiO 2 addition on the sintering behavior, phase composition, microstructure and microwave dielectric properties were investigated systematically. The dense microstructure could be obtained in low TiO 2 content (x=0.1) samples sintered at 1100 °C. The dielectric constant ε r was attributed to the bulk density and TiO 2 content. The variation in Q×f values is related to the bulk density, and improved values could be obtained for Li 3 Mg 2 NbO 6 –0.1TiO 2 ceramics. The quality factor (Q×f) had a maximum for x=0.1 and the temperature coefficient of resonant frequency (τ f ) value shifted towards positive direction with the increase of TiO 2 addition. Notably, Li 3 Mg 2 NbO 6 –0.1TiO 2 ceramics sintered at 1100 °C possessed excellent microwave dielectric properties: ε r =15, Q×f =74,000 GHz(9.93GHz), τ f = −3.4 ppm/°C, which made the ceramics as promising low loss and temperature stable candidates for millimeter-wave applications.
What problem does this paper attempt to address?