Investigation on the effect of reactive (CuO) and non-reactive (3YSZ) additives on dielectric and mechanical properties of MgTiO3
Dehghaniyan, Seyed Farzad
DOI: https://doi.org/10.1007/s10854-024-13698-8
2024-10-18
Journal of Materials Science Materials in Electronics
Abstract:The investigation in this study focused on the microstructure, mechanical strength, and microwave dielectric properties of novel MgTiO 3 composites containing different amounts of CuO and 3YSZ. The synthesis of the MgTiO 3 compound was carried out using the conventional solid-state reaction method, while the composites were fabricated through wet mixing, pressing in a die, and sintering in air at temperatures ranging from 1200 to 1350 °C for a duration of 5 h. Density measurements by Archimedes method, indicated that the addition of 3 wt% of both additives led to an improvement in the densification behavior of MgTiO 3 . X-ray analysis of the sintered samples confirmed that the reaction between CuO and MgTiO 3 resulted in the formation of the Mg 2 TiO 4 phase, while 3YSZ exhibited good chemical stability and acted as a secondary phase. The incorporation of CuO and 3YSZ effectively enhanced the mechanical properties of the MgTiO 3 ceramics. Specifically, the MgTiO 3 ceramics mixed with 1 wt% CuO and 5 wt% 3YSZ demonstrated excellent mechanical and dielectric properties, with a fractural strength (σ b ) of 90 and 70 MPa, Vickers hardness (HV) of 870 and 845, relative permittivity (ε r ) of 17.3 and 17.2, and quality factor (Q*f) of 174,000 and 166,000 GHz for 1 wt% CuO and 3 wt% YSZ, respectively.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied