Abstract:To explore the W nanoparticles effects on the subsurface microstructural self-organization of Cu-Ag two-phase alloys and the resulting wear performance, we have fabricated bulk nanostructured Cu-10 at% Ag-10 at% W ternary alloys by high energy ball milling and warm pressing. During ball milling, Ag is dissolved into the Cu matrix but W remains immiscible. Compaction of the powders into bulk at 300 °C leads to the Ag precipitation. The as-pressed Cu-10 at% Ag-10 at% W ternary alloy has Ag-rich precipitates size (dAg) of 22 nm and W particles size (dw) of 26 nm. Further annealing at 600 °C for 1 h only increases dAg and dw to 52 nm and 41 nm, respectively. The fabricated Cu-10 at% Ag-10 at% W ternary alloys thus demonstrate enhanced coarsening resistance. The two alloys were then subjected to dry sliding wear against stainless steel disks. It is found that the initial length scale of Ag-rich precipitates and W particles has a profound influence on the microstructure evolution during wear and accordingly on the wear performance. For the as-pressed sample with small dAg and dW, severe plastic deformation (SPD) by wear forced the formation of Cu-Ag homogeneous solid solution, leading to low wear resistance. In contrast, for the annealed one with relatively large dAg and dW, the Cu, Ag and W three phases co-existed but the Ag-rich precipitates were transformed into wavy nanolayers, providing enhanced wear resistance. Compared with Cu-Ag alloys subjected to sliding wear, the presence of W nanoparticles was found to hinder the formation of self-organized nanolayered structure and leads to a small deformation depth. The obtained results provide deep insights into the plastic deformation mechanisms in ternary alloys and the design of wear resistant engineering materials.

Microstructure, sliding wear and corrosion behavior of bulk nanostructured Co-Ag immiscible alloys

Microstructure and Corrosion Resistance of Medical Cobalt-Based Alloys

Reforming Nanostructured CuAg Alloy to Improve Ductility and Electrical Conductivity

Nanoscale self-organization reaction in Cu-Ag alloys subjected to dry sliding and its impact on wear resistance

Effects of nanocrystalline microstructure on the dry sliding wear behavior of a Cu-10 at% Ag-10 at% W ternary alloy against stainless steel

Sliding Wear Induced Subsurface Microstructural Evolution in Nanocrystalline Nb-Ag Binary Alloys and Its Impact on Tribological Performance

A Strong, Wear- and Corrosion-Resistant, and Antibacterial Co–30 At.% Cr–5 At.% Ag Ternary Alloy for Medical Implants

Tribological and Corrosion Behaviors of Bulk CuW Nanocomposites Fabricated by Mechanical Alloying and Warm Pressing

Microstructure, Mechanical Properties, and Corrosion Behavior of Al-4.0Cu-1.1Li-0.5Mg-xAg Alloys

Microstructure and Dry Sliding Wear Behavior of Ultrafine-Grained Co-30 At% Cr Alloy at Room and Elevated Temperatures

Effects of micro-alloying Ag on microstructure, mechanical properties and corrosion behavior of extruded Mg-2Zn-0.2Ca-xAg alloys

Microstructure and Wear Properties of Al-Based Bearing Alloys Fabricated by Mechanical Alloying

Excellent Corrosion and Wear Resistance of Amorphous and Crystalline ZrCoAl Alloys

Sliding wear-induced chemical nanolayering in Cu–Ag, and its implications for high wear resistance

Sliding Wear of Nanocrystalline Nb-Ag at Elevated Temperatures: Evolution of Subsurface Microstructure and Its Correlation with Wear Performance

Effect of surface microstructure for corrosion resistance and magnetic properties of an amorphous cobalt-based Co-Si-Fe-Cr-Al ALLOY

Fabrication, Tribological and Corrosion Behaviors of Ultra-Fine Grained Co–28Cr–6Mo Alloy for Biomedical Applications

Microstructure evolution and deformation mechanism of coherent L12-strengthened high-entropy alloy during sliding wear

Microstructural changes and dry sliding wear behavior of Cu-15Ni-8Sn-0.5Co alloy during deformation and aging treatment

Microstructure and tribological properties of electrodeposited Ni–Co alloy deposits

Electrochemical Behavior of Cobalt-Based Nanostructured Amorphous Alloys in Alkaline Solution