Abstract:The present work aims to examine the reciprocating wear characteristics at elevated temperatures (200 °C, 400 °C, and 600 °C) of CoCrFeNiW 0.3 + 5 at% C high entropy alloy coatings, which has been synthesized by atmospheric plasma spraying. The experimental findings pertaining to the worn surface demonstrate that an increase in testing temperature leads to a reduction in wear scar depth. The findings derived from the examination using field emission scanning electron microscopy (FESEM) revealed the existence of wear debris, an adhesive layer, craters, and scratches on the surfaces that were subjected to wear. The examination of worn surfaces using X-ray photoelectron spectroscopy (XPS) has shown the existence of several oxides. The presence of oxides is established while evaluating worn surfaces by Fourier transform infrared spectroscopy (FTIR). The X-ray diffraction (XRD) analysis reveals that the lack of oxide development might perhaps be attributed to the limited width of the worn track. The observed reduction in wear volume loss with increasing testing temperature may be attributable to the reaction arise inside the tribolayer and oxides formation. The energy-dispersive X-ray spectroscopy (EDS) examination of the Al 2 O 3 counter body indicated the presence of a transferred tribofilm. The alloy coating, namely the CoCrFeNiW 0.3 + 5 at% C alloy coating, exhibits a decreased mass loss of 9.43 mg and an average coefficient of friction of 0.46 at a test temperature of 600 °C. When the sample is subjected to a wear testing temperature of 600 °C, the wear mass is decreased by 24.37%. The results of this investigation provide promising prospects for practical use in applications requiring high temperature wear resistance.

Microstructure and Dry Sliding Wear Behavior of Ultrafine-Grained Co-30 At% Cr Alloy at Room and Elevated Temperatures

On the enhanced wear resistance of CoCrFeMnNi high entropy alloy at intermediate temperature

Microstructure evolution and deformation mechanism of coherent L12-strengthened high-entropy alloy during sliding wear

Insights into the microstructural evolution and wear behavior of underwater friction stir processed CoCrFeNiMn high-entropy alloy

Microstructures and Mechanical Properties of a L12-structured Precipitation Strengthened Co-based Superalloy

Achieving low wear in a complex concentrated alloy CrFeNiNb with multi-phase hierarchical microstructure

Room and Elevated Temperature Sliding Friction and Wear Behavior of Al0.3CoFeCrNi and Al0.3CuFeCrNi2 High Entropy Alloys

Effect of C additions to the microstructure and wear behaviour of CoCrFeNi high-entropy alloy

High temperature tribological behavior of atmospheric plasma-sprayed CoCrFeNiW0.3 + 5 at% C high-entropy alloy coating

Wear-resistant CoCrNi multi-principal element alloy at cryogenic temperature

Microstructure evolution and mechanical properties of CoCrFeNiAl0.3 high entropy alloy produced by ball milling in combination with thermomechanical consolidation

Microstructure and wear mechanism of CoCrCuFeNiVx high entropy alloy by sintering and electron beam remelting

The sliding wear behaviour of CoCrFeMnNi and AlxCoCrFeNi high entropy alloys at elevated temperatures

Preparation and Properties of Ultra-High Hardness Co-Cr-Mo-Nb-B High-Temperature Amorphous Alloy Coating

Friction-induced rapid amorphization in a wear-resistant (CoCrNi) 88 Mo 12 dual-phase medium-entropy alloy at cryogenic temperature

Achieving low wear in a μ-phase reinforced high-entropy alloy and associated subsurface microstructure evolution

Wear-resistant CrCoNi nanocrystalline film via friction-driven surface segregation

Microstructure Characteristics and Elevated-Temperature Wear Mechanism of FeCoCrNiAl High-Entropy Alloy Prepared by Laser Cladding

Microstructure, Mechanical Properties, and Sliding Wear Behavior of Oxide-Dispersion-Strengthened FeMnNi Alloy Fabricated by Spark Plasma Sintering

Improvement of Microstructure and Sliding Wear Property of Cold-Sprayed FeAl Intermetallic Compound Coating by Annealing Treatment

Simultaneously enhancing mechanical and tribological performance in undercooled Co-18.5 at. % B alloys