Abstract:Direct-ink-writing (DIW)-based 3D-printing technology combined with the direct-foaming method provides a new strategy for the fabrication of porous materials. We herein report a novel method of preparing porous SiC ceramics using the DIW process and investigate their mechanical and wave absorption properties. We investigated the effects of nozzle diameter on the macroscopic shape and microstructure of the DIW SiC green bodies. Subsequently, the influences of the sintering temperature on the mechanical properties and electromagnetic (EM) wave absorption performance of the final porous SiC-sintered ceramics were also studied. The results showed that the nozzle diameter played an important role in maintaining the structure of the SiC green part. The printed products contained large amounts of closed pores with diameters of approximately 100–200 μm. As the sintering temperature increased, the porosity of porous SiC-sintered ceramics decreased while the compressive strength increased. The maximum open porosity and compressive strength were 65.4% and 7.9 MPa, respectively. The minimum reflection loss (RL) was −48.9 dB, and the maximum effective absorption bandwidth (EAB) value was 3.7 GHz. Notably, porous SiC ceramics after sintering at 1650 °C could meet the application requirements with a compressive strength of 7.9 MPa, a minimum RL of −27.1 dB, and an EAB value of 3.4 GHz. This study demonstrated the potential of direct foaming combined with DIW-based 3D printing to prepare porous SiC ceramics for high strength and excellent EM wave absorption applications.

Porous (Sicw-Si3n4w)/(si3n4-sic) Composite with Enhanced Mechanical Performance Fabricated by 3D Printing

3D-SiC decorated with SiC whiskers: Chemical vapor infiltration on the porous 3D-SiC lattices derived from polycarbosilane-based suspensions

Fabrication and characterization of carbon fiber reinforced SiC ceramic matrix composites based on 3D printing technology

Microstructures, Mechanical Properties and Electromagnetic Wave Absorption Performance of Porous SiC Ceramics by Direct Foaming Combined with Direct-Ink-Writing-Based 3D Printing

Mechanical and dielectric properties of porous and wave-transparent Si3N4-Si3N4 composite ceramics fabricated by 3D printing combined with chemical vapor infiltration

Thermally assisted extrusion-based 3D printing of continuous carbon fiber-reinforced SiC composites

Preparation and Mechanical Performance of SiCw/geopolymer Composites Through Direct Ink Writing

Silicon carbide whiskers reinforced SiOC ceramics through digital light processing 3D printing technology

Fabrication of High‐strength Porous SiC‐based Composites with Unidirectional Channels

Fabrication of Bamboo-Inspired Continuous Carbon Fiber-Reinforced SiC Composites Via Dual-Material Thermally Assisted Extrusion-Based 3D Printing

Fabrication of Si3N4–SiC/SiO2 composites using 3D printing and infiltration processing

3D Printing of Honeycomb Si3N4 Ceramic

Fabrication and characterization of SiC whisker reinforced reaction bonded SiC composite

The properties of the multi-node SiCw and its reinforced Si 3N4 ceramic composite material

Direct Ink Writing of Chopped Carbon Fibers Reinforced Polymer-derived SiC Composites with Low shrinkage and High Strength

Mullite-bonded SiC-whisker-reinforced SiC Matrix Composites: Preparation, Characterization, and Toughening Mechanisms

Fabrication of dense Cf/SiC ceramic matrix composites using 3D printing and PIP with short carbon fibre as a toughening material

High-strength and low-silicon SiC ceramics prepared by extrusion molding 3D printing

Microstructure and mechanical properties of continuous carbon fiber-reinforced SiC ceramic composite fabricated by direct ink writing

3D printing of fibre-reinforced ceramic composites with hierarchical structure

Si3N4-SiC Composite Ceramic Prepared by Three Dimensional Printing and Chemical Vapor Infiltration