Mullite-bonded SiC-whisker-reinforced SiC Matrix Composites: Preparation, Characterization, and Toughening Mechanisms

Yang Luo,Shi-li Zheng,Shu-hua Ma,Chun-li Liu,Xiao-hui Wang

DOI: https://doi.org/10.1016/j.jeurceramsoc.2018.08.022

IF: 5.7

2018-01-01

Journal of the European Ceramic Society

Abstract:A novel mullite-bonded SiC-whisker-reinforced SiC matrix composite (SiCw/SiC, SiC whisker-to-SiC powder mass ratio of 1:9) was designed and successfully prepared. Before preparing the composite, the inexpensive lab-made SiCw was first modified by an oxidation/leaching process and then coated with Al2O3. The kinetics results indicate that the oxidation process can be described by improved shrinking-cylinder models. The aspect ratio of SiCw improved after modification. Subsequently, raw materials with a SiC-SiO2-Al2O3 triple-layered structure were obtained after the Al2O3-coating process and used as feedstocks during the subsequent hot-pressing sintering. Finally, the characterization of the composites indicates that the mullite-bonded sample performs better (relative density of 93.8 +/- 1.4%, flexural strength of 533.3 +/- 18.2 MPa, fracture toughness of 13.6 +/- 2.1 MPa m(1/2), and Vickers hardness of 20.6 +/- 2.5 GPa) than the reference sample without the mullite interface. The improved toughness could essentially be attributed to the moderately strong interface bonding and effective load transfer effects of the mullite interface.