Abstract:The thermal shock damage behavior of SiC/SiC‐EBC is systematically investigated. Coating cracking or even peeling occurs due to thermal stress mismatch, which acts as channels for oxygen, leading to oxidative damage of Si coatings and partial SiC/SiC substrate. However, delamination within SiC/SiC substrate is the main cause of SiC/SiC‐EBC failure. Thermal shock damage is a key issue for the stable service of SiC/SiC with environmental barrier coating (EBC) in aero‐engines. The thermal shock damage behavior of SiC/SiC with barium‐strontium aluminosilicate (BSAS)‐based EBC in an air atmosphere quenched by air and water media between RT and 1200 °C is systematically investigated. After 600 thermal shock cycles, cracks form in the EBC due to a sharp increase in the internal thermal stresses, and a SiO2 TGO layer is formed on the Si bonding coat. Based on the TGO thickness, damage within BSAS/mullite coatings is quantified by the oxygen permeability (2.541 × 10−11 mol·(atm cm s)−1), which is increased by 2.5 times compared to static oxidation. Despite cracking damage occurring in the SiC matrix of SiC/SiC substrates, the load‐bearing capability of SiC fibers is improved due to the modulus matching of the fiber/matrix. Oxidation damage is dominated the degradation of the performance of SiC/SiC substrates, whose flexural strength is decreased by 15% after 600 cycles. In the thermal shock test quenched by water media, the strength retention of SiC/SiC‐EBC is below 60%, and an increase in internal defects and even delamination of the SiC/SiC substrate are the main reasons for the thermal shock failure of SiC/SiC‐EBC.

Cracking Behavior of ZrB2-SiC-Graphite Sharp Leading Edges During Thermal Shock

Thermal Shock Behavior of Al2O3/TiO2-NiCrBSi Graded Thermal Barrier Coatings Produced by Flame Spraying

Thermal Shock Performance of CVD Tungsten Coating at Elevated Temperatures

Influence of Surface Morphology and Microstructure on Performance of CVD Tungsten Coating under Fusion Transient Thermal Loads

Wear Behaviour and Microstructural Changes of SiCw-Al Composite under Unlubricated Sliding Friction

Experiment and Prediction of Crack Spacing of ZnS under Thermal Shock

Thermal shock behavior of SiC-whisker-reinforced diboride ultrahigh-temperature ceramics

An Aqueous Polymer Quenching Medium for Instantaneous Thermal Shock Cooling Rate Study of Ceramic Materials

Effect of repeated thermal shock on mechanical properties of ZrB2-SiC-BN ceramic composites

Thermal Shock Behavior of Zrb2-Sic Ceramics with Different Quenching Media

Failure behavior of SiC/SiC with BSAS-based EBC in gas combustion environment

Properties evolution and damage mechanism of SiC/SiC composites after thermal shock at 1300 °C

Rapid Heating Thermal Shock Behavior Study of CVD ZnS Infrared Window Material: Numerical and Experimental Study

Thermal Shock Damage and Failure Mechanism of 2D Laminated SiC/SiC with Barium‐Strontium Aluminosilicate‐Based Environmental Barrier Coating

Experiment and simulation analysis on thermal shock resistance of laminated ceramics with graphite and boron nitride interfaces

Thermal Shock Resistance for YSZ Thermal Barrier Coating Materials

Sintering governing the cracking behaviors of different La2Zr2O7/YSZ ceramic layer combination TBCs at 1150 °C

Effect of Surface Heat Transfer Coefficient Gradient on Thermal Shock Failure of Ceramic Materials under Rapid Cooling Condition

Surface Damage Evolution During Transient Thermal Shock of W-2%vol Y2O3 Composite Material in Different Surfaces

Microstructure Evolution and Impedance Analysis of 7YSZ Thermal Barrier Coating During Gas Thermal-Shock

Microstructure, surface stress and surface temperature response of ZrB2–SiC based coatings