Abstract:CuW composites were synthesized using an equal channel angular pressing (ECAP) technique. Microstructural evolution during sintering process was investigated using both optical microscopy and transmission electron microscopy (TEM), and their deformation mechanisms were studied using finite element analysis (FEA). Results showed severe plastic deformation of the CuW composites and effective refinement of W grains after the ECAP process. TEM observation revealed that the ECAP process resulted in lamellar bands with high densities dislocations inside the composites. Effects of extrusion temperature and extrusion angles on stress-strain relationship and sizes of deformation zones after the ECAP process were investigated both theoretically and experimentally. When the extrusion angle was 90 degrees, a maximum equivalent stress of-1001 MPa was obtained when the extrusion test was done at room temperature of 22 degrees C, and this value was lower than compression strength of the CuW composites (1105.43 MPa). The maximum equivalent strains were varied between 0.5 and 0.7. However, when the extrusion temperature was increased to 550 degrees C and further to 900 degrees C, the maximum equivalent stresses were decreased sharply, with readings of 311 MPa and 68 MPa, respectively. When the extrusion angle was increased to 135 degrees, the maximum equivalent stresses were found to be 716.9 MPa, 208 MPa, and 32 MPa for the samples extruded at temperatures of 22 degrees C, 550 degrees C and 900 degrees C, respectively. Simultaneously, the maximum equivalent strains were decreased to 0.2-0.4. Furthermore, results showed that the maximum equivalent stress was located on the sample's external surface and the stress values were gradually decreased from the surface to the center of samples, and the magnitudes of plastic deformation zones at the surface were much larger than those at the central part of the sintered samples. FEA simulation results were in good agreements with experimentally measured ones. (c) 2018 Elsevier Ltd. All rights reserved.

Experimental and Theoretical Analysis of Microstructural Evolution and Deformation Behaviors of CuW Composites During Equal Channel Angular Pressing

Long-term Ball Milling and Hot Pressing of In-Situ Nanoscale Tungsten Carbides Reinforced Copper Composite and Its Characterization

Tensile Deformation Behaviors of CuNi Alloy Processed by Equal Channel Angular Pressing

Tensile and Compressive Deformation Behaviors of Commercially Pure Al Processed by Equal-Channel Angular Pressing with Different Dies

Microstructure and high-temperature mechanical properties of Cu-W composite prepared by hot isostatic pressing

Co-deformation in Cu–6 Wt.% Ag Nanocomposites

Enhancing mechanical properties and microstructure evolution of hybrid AZ61-5SiC-0.5CNTs composite during equal channel angular pressing

The W alloying effect on thermal stability and hardening of nanostructured Cu-W alloyed thin films

Experimental Investigation of Tensile Properties and Fracture Mechanism of WCP/Cu Composites Reinforced with Different WCP Volume Fraction

Electron Backscatter Diffraction Investigation on Microstructure Evolution of TiB2(p)/Al-Cu Composite after Single-Pass Equal Channel Angular Pressing for Formability Assessment

Structural Characterization of Binary Al-Cu Alloy Processed by Equal Channel Angular Pressing at Half of the Melting Point

Experimental and Numerical Investigation of the ECAP Processed Copper: Microstructural Evolution, Crystallographic Texture and Hardness Homogeneity

Insight into the Microstructure and Tensile Behavior of the W–Cu Composite Reinforced with Tungsten Fibers and Particulates

Characterization of microstructural evolution and mechanical properties of Cu-Ni-Cr alloys deformed by ECAP

Ebsp Investigation of Microstructure and Texture Evolution During Equal Channel Angular Pressing of Aluminium

Investigating the effect of WC reinforcements in Cu Ti composite filler on the microstructural evolution and mechanical characteristics in brazing C f /SiC and GH3536

Microstructure, mechanical properties and arc erosion behavior of CuW composites prepared by high energy ball milling and spark plasma sintering

The Effect of Severe Plastic Deformation on the Microstructure and Mechanical Properties of (tib+tic) Reinforced Titanium Matrix Composites

Study of a New Method to Fabricate W–Cu Composites

Fracture Behavior of Cu/Cu–WCP Layered Composites

Numerical investigations on the hybrid effect and deformation mechanism of TiB2p and TiBw reinforced Cu composites prepared by in-situ mixing casting