Abstract:TixCr1 - yFeyMn1.0 (x = 1.02, 1.05, 1.1, 0.05 <= y <= 0.25) alloys were prepared by plasma arc melting and annealing at 1273 K for 2 hours. The XRD results show that the main phase of all alloys is the C14 type Laves phase, and a little secondary phase exists in a mixture of the binary alloy phase. The lattice parameters increase with Ti super-stoichiometry ratio increasing, whereas smaller lattice parameters emerge with increasing Fe stoichiometry content. Additionally, as the Ti super-stoichiometry ratio decreases, the pressure-composition-temperature measurements indicated that hydrogen absorption and desorption plateau pressures of TixCr0.9Fe0.1Mn1.0 (x = 1.1, 1.05, 1.02) alloys increase from 3.15, 0.67, to 5.94, 1.13 MPa at 233 K, respectively. On the other hand, with the Fe content increasing in Ti1.05Cr1 - yFeyMn1.0 (0.1 <= y <= 0.25) alloys from 0.1 to 0.25, the hydrogen desorption plateau pressures increased from 1.41 to 2.46 MPa at 243 K. The hydrogen desorption plateau slopes reduce to 0.2 with Ti super-stoichiometry ratio decreasing to 1.02, but the alloys are very difficult to activate for hydrogen absorption and cannot activate when the Fe substituting for Cr exceeds 0.2. The maximum hydrogen storage capacities were more than 1.85 wt% at 201 K. The reversible hydrogen storage capacities can remain more than 1.55 wt% at 271 K. The enthalpy and entropy for all hydride dehydrogenation are in the range of 21.0 to 25.5 kJ/mol H-2 and 116 to 122 J mol(-1) K-1, respectively. Our results suggest that Ti1.05Cr0.75Fe0.25Mn1.0 alloy with low enthalpy holds great promise for a high hydrogen pressure hybrid tank in a hydrogen refueling station (45 MPa at 333 K), and the other alloys of low cost may be used for a potable hybrid tank due to high dissociation pressure at 243 K and high volumetric density exceeding 40 kg/m(3).

Hydrogen Storage Properties Of(ti 0.85 Zr 0.15 ) 1.05 Mn 1.2 Cr 0.6 V 0.1 M 0.1 （m=ni,fe,cu） Alloys Easily Activated at Room Temperature

Hydrogen storage capabilities of the alloys Fe 0.85Mn 0.15Ti 0.9M 0.1 (M=Zr, V, Ca)

Development of Ti–Zr–Mn–Cr-(V–Fe) Based Alloys for Hydrogen Feeding System in Hydrogen Metallurgy Application

Experimental and Theoretical Investigation on the Enhanced Hydrogen Storage Performance of Ti–Cr–Mn–Fe-Based Alloys Modified by Nb Substitution

Hydrogen Storage Properties of Ti-Cr-Mn-M (M=V, Fe, Ni, Cu) Alloys

Hydrogen Storage Properties and Crystal Structure of Ti-Cr Based Alloys

Hydrogen storage properties of TiMn2-based alloys

Effects of the Different Element Substitution on Hydrogen Storage Properties of Ti0.8Zr0.2Mn0.9Cr0.6V0.3M0.2 (M = Fe, Ni, Co)

Microstructures and Hydrogen Storage Properties of Ti10V83-xFe6ZrMnx Alloys

Phase Structures and Hydrogen Storage Properties of TiV1.35Cr1.35-xMnx Alloys(x=0～0.45)

Microstructure and hydrogen storage properties of Ti10+xV80-xFe6Zr4 (x=0~15) alloys

Effect of different metal element substitution on microstructural and comprehensive hydrogen storage performance of Ti0·9Zr0·1Mn0·95Cr0·7V0.2M0.15 (M = Fe, Co, Ni, Cu, Mo) alloy

Microstructure and Electrochemical Properties of V_(2.1)TiNi_(0.4)Zr_(0.06)Cu_(0.03)M_(0.10)(M=Cr, Co, Fe, Nb, Ta) Hydrogen Storage Alloys

Hydrogen storage properties of V+TiFe0.85Mn0.15 multi-phase alloys

Development of Ti-Zr-Mn-Cr-V based alloys for high-density hydrogen storage

Microstructure and Electrochemical Properties of V2.1TiNi0.4Zr0.06Cux (X=0-0.12) Hydrogen Storage Alloys

Phase structures and hydrogen storage properties

Phase Structure and Hydrogen Storage Properties of Ti17cr23v55-Xzr5fex (X=11 Similar to 16) Alloys

Hydrogen storage performances, kinetics and microstructure of Ti<sub>1.02</sub>Cr<sub>1.0</sub>Fe<sub>0.7-x</sub>Mn<sub>0.3</sub>Al<su b>x</sub> alloy by Al substituting for Fe

High-Pressure Hydrogen Storage Properties Of Tixcr1-Yfeymn1.0 Alloys

Influence of the Substitution Cr for Mn on Structural and Hydrogen Storage Performance of Ti 0.9 Zr 0.1 V 0.45 Cr X Mn 1.5-X (x=0, 0.05, 0.1, 0.15, 0.2) Alloys