Abstract:Abstract The synthesis, microstructure, and properties of high purity dense bulk Mo 2 TiAlC 2 ceramics were studied. High purity Mo 2 TiAlC 2 powder was synthesized at 1873 K starting from Mo, Ti, Al, and graphite powders with a molar ratio of 2:1:1.25:2. The synthesis mechanism of Mo 2 TiAlC 2 was explored by analyzing the compositions of samples sintered at different temperatures. It was found that the Mo 2 TiAlC 2 phase was formed from the reaction among Mo 3 Al 2 C, Mo 2 C, TiC, and C. Dense Mo 2 TiAlC 2 bulk sample was prepared by spark plasma sintering (SPS) at 1673 K under a pressure of 40 MPa. The relative density of the dense sample was 98.3%. The mean grain size was 3.5 μm in length and 1.5 μm in width. The typical layered structure could be clearly observed. The electrical conductivity of Mo 2 TiAlC 2 ceramic measured at the temperature range of 2–300 K decreased from 0.95 × 10 6 to 0.77 × 10 6 Ω–1·m–1. Thermal conductivity measured at the temperature range of 300–1273 K decreased from 8.0 to 6.4 W·(m·K) –1 . The thermal expansion coefficient (TEC) of Mo 2 TiAlC 2 measured at the temperature of 350–1100 K was calculated as 9.0 × 10 –6 K –1 . Additionally, the layered structure and fine grain size benefited for excellent mechanical properties of low intrinsic Vickers hardness of 5.2 GPa, high flexural strength of 407.9 MPa, high fracture toughness of 6.5 MPa·m 1/2 , and high compressive strength of 1079 MPa. Even at the indentation load of 300 N, the residual flexural strength could hold 84% of the value of undamaged one, indicating remarkable damage tolerance. Furthermore, it was confirmed that Mo 2 TiAlC 2 ceramic had a good oxidation resistance below 1200 K in the air.

Synthesis and Microstructure of Ti2AlN Ceramic by Thermal Explosion

Rapid Synthesis of Ti2aln Ceramic Via Thermal Explosion

Rapid Synthesis of MoAlB Ceramic Via Thermal Explosion

Tem Investigation on Ceramic Strengthening Nial-Based Composite Prepared by Thermal Explosion and Hot Extrusion

One-step sintering of porous TiAl3 intermetallics using TiH2 as raw material in thermal explosion reaction

Preparation of Mn2AlB2 Material via Thermal Explosion

Combustion Synthesis and Thermal Stability of Ti3AlC2

Reaction Behavior of Porous TiAl3 Intermetallics Fabricated by Thermal Explosion with Different Particle Sizes

Preparation and properties of Al2O3/Al-2(1-0.2)Mg0.2Ti(1+0.2)O5 matrix ceramic composite

COMBUSTION SYNTHFSIS AND DENSIFICATION BY GAS HOT ISOSTATIC PRESSURE OF AIN- TiB2 CERAMIC WITHOUT ENVELOPE

Microstructural Evolution During Self-Propagating High Temperature Synthesis of Ti2AlC Machinable Ceramics

Combustion Synthesis of NiAl/TiC Multiphase Composites and their Related Microstructure

Highly Textured Ti2AlN Ceramic Prepared Via Thermal Explosion Followed by Edge-Free Spark Plasma Sintering

A synthesis method of Ti3AlC2 ceramic

Synthesis, microstructure, and properties of high purity Mo2TiAlC2 ceramics fabricated by spark plasma sintering

Efficient and cost-effective method to synthesize highly purified Ti4AlN3 and Ti2AlN

Effect of Reaction Atmosphere on Combustion Synthesis of Ti2AlN

Efficient and cost-effective method to synthesize highly purified Ti<sub>4</sub>AlN<sub>3</sub> and Ti<sub>2</sub>AlN

Microstructures, Densification and Mechanical Properties of TiC–Al2O3–Al Composite by Field-Activated Combustion Synthesis

Formation mechanism of Ti3AlC2 in TiO2–Al–C/TiC systems at high temperatures

Microstructure and Mechanical Properties of Ni3Al Fabricated by Thermal Explosion and Hot Extrusion