Temperature Stable Microwave Dielectric Ceramics in Li1.33xZn2-2xTi1+0.67xO4 (0.75 < X < 1) Cubic Spinels and Their Chemical Compatibility with Silver

Weishuang Fang,Yanming Sun,Liang Fang,Ying Tang,Chunchun Li

DOI: https://doi.org/10.1016/j.jallcom.2017.06.033

IF: 6.2

2017-01-01

Journal of Alloys and Compounds

Abstract:A series of microwave dielectric ceramics in Li1.33xZn2-2xTi1+0.67xO4 (x = 0.8, 0.9, 0.95) system prepared by a solid-state reaction method were reported. Raman spectroscopy was employed to investigate the structure and microwave dielectric properties. Dense ceramics were obtained at relatively low sintering temperatures (940-1040 degrees C). As x increased, the sintering temperature decreased from 1040 degrees C at x = 0.8, to 960 degrees C at x = 0.9, and then to 940 degrees C at x = 0.95. The microwave dielectric properties of Li1.33xZn2-2xTi1+0.67xO4 were found to be sensitive to the composition and densification. A ceramic with x = 0.95 exhibited reasonably good microwave dielectric properties with epsilon(r) = 26.4, Q x f = 16,040 GHz and r(f) = 5.3 ppmf degrees C when sintered at 940 degrees C. The chemical compatibility with silver of the x = 0.95 sample was evaluated for LTCC applications. (C) 2017 Elsevier B.V. All rights reserved.