Combined effect of rattling and compression on the microwave dielectric properties of B-site 1:3 ordered Li6A7Ti11O32 (A = Zn, Mg) spinels

Mu Li,Ying Tang,Huaicheng Xiang,Jie Li,Di Zhou,Liang Fang

DOI: https://doi.org/10.1016/j.ceramint.2022.11.021

IF: 5.532

2023-03-01

Ceramics International

Abstract:Dense ceramics of two B-site 1:3 ordering spinels Li6A7Ti11O32 (A = Zn, Mg) with space group P4332 were prepared by solid-state reaction. Raman spectroscopy and XRD analysis revealed why the lattice parameters and volume of Li6Mg7Ti11O32 are abnormally greater than those of Li6Zn7Ti11O32. Li6Zn7Ti11O32 exhibits outstanding microwave dielectric properties (Q × f = 129,600 GHz (8.9 GHz), ε r  = 20.7, τ f  = −45 ppm/°C) and a low thermal expansion coefficient (α L ) of 5.5 ppm/°C. While Mg-analogue displayed a lower Q × f ∼108,600 GHz (9.1 GHz), a lower α L  ∼ 4.9 ppm/°C, a higher ε r  ∼ 21.9, and a slightly positive offset τ f  ∼ −21 ppm/°C relative to Li6Zn7Ti11O32. A significant positive deviation of 91.6% was observed between the corrected ε r(corr) by the porosity and the calculated ε r(C-M) by the Clausius-Mosotti (C-M) equation in the Li1.33x A2-2x Ti1+0.67x O4 solid solution. The variation in ε r and τ f values of Li6A7Ti11O32 (x = 0.5625) compared to Li2ATi3O8 (x = 0.75) might be attributed to the combined effect of rattling and compression cations at A-site and B-site. Moreover, the negative τ f of Li6A7Ti11O32 (A = Zn, Mg) ceramics was balanced to near zero by adding CaTiO3.

materials science, ceramics