Preferential site occupancy, octahedral stabilization energy, and microwave dielectric properties of mixed spinel Mg0.95X0.05Al2O4

Fengsheng Zeng,Jiuyuan Han,Guoyun Shao,Rengang Shi,Raz Muhammad,Yuanyuan Zhang,Fayaz Hussain,Hadi Barzegar Bafrooei,Ehsan Taheri-Nassaj,Kaixin Song

DOI: https://doi.org/10.1016/j.ceramint.2024.01.422

IF: 5.532

2024-02-01

Ceramics International

Abstract:In this paper, different divalent ions (X = Ni, Cu, Mg, Co, Zn) are doped to replace Mg2+ at the tetrahedral sites in mixed spinel Mg0.95X0.05Al2O4. These substitutions induce variations in the degree of inversion/preferential occupation at the A/B lattice site in MgAl2O4 ceramics because the octahedral stabilization energies change as a function of dopant. According to crystal field theory, the number of d-orbital electrons has a significant impact on the stability of octahedral sites. Therefore, OSPE values vary between 0 Dq and 0.845 Dq for different elements. The higher the OSPE value, the greater the degree of inversion, and the higher the quality factor (Q×f). The dielectric constant (ε r) and temperature coefficient of resonant frequency ( τ f ) of Mg0.95X0.05Al2O4 ceramics changes as a function of the ionic polarizability and B-site bond valence. Mg0.95Ni0.05Al2O4 with a higher OSPE (8.45 Dq) and degree of inversion of A/B sites (λ = 0.221), has the better set of microwave dielectric properties (ε r = 8.39, Q×f = 78,338 GHz, τ f  = −66.8 ppm/°C). The adjustment of stability energy of octahedral sites is favorable to improve the microwave dielectric properties of MgAl2O4 spinel.

materials science, ceramics