Abstract:Abstract Mullite porous ceramics with high porosity and good mechanical properties were prepared by foaming method combined with gel casting process using kaolin and alumina as main raw materials and sodium polyoxyethylene ether sulfate as foaming agent. The effects of sintering process and magnesium oxide content on the microstructure and properties of mullite porous ceramics were investigated. The studies show that: With the addition of magnesium oxide, the amount of mullite produced and the compactness of the sample will increase. At this time, the microscopic morphology of mullite is needle-like and prismatic, and the mechanical properties are better. and the pore size distribution gradually tends to be between 0.1-0.2mm and 0.2-0.3mm. The addition of magnesium oxide, The amount of mullite phase increased, the densification degree of the sample increased, and the acicular and prismatic mullite phases with good mechanical properties were mainly formed, and the porosity of mullite porous ceramics decreased and the compressive strength increased. The pore size distribution gradually tends to be between 0.1-0.2mm and 0.2-0.3mm. As the sintering temperature increases, the porosity of mullite porous ceramics decreases and the compressive strength increases. With the extension of the holding time, the amount of mullite phase generated increases, the porosity remains basically unchanged, and the compressive strength increases.

The Effect of Sintering Atmosphere and C/U on UCO Microspheres by Internal Gelation Process with Carbon Black

Fabrication Process Study of UCO Composite Ceramic Microspheres with Fructose As a Carbon Source by Internal Gelation and Carbothermic Reduction

The Effects of Carbon Content on ZrCO Microspheres Prepared by Internal Gelation Process with Carbon Black

The Study of Carbothermic Reduction–sintering of ZrO2–ZrC–C Composite Microspheres Prepared by Internal Gelation

Preparation of UCO Microspheres by Internal Gelation Process

Sintering of UO_2 Microsphere and Its Performance

Sintering of UO2 Microsphere and Its Performance

Effect of Carbon Powder on ZrC ZrO2 Microspheres Prepared by Internal Gelation Process

The Preparation of ZrO2–ZrC Ceramic Microspheres by Internal Gelation Process with Sucrose As a Carbon Source

Effect of UV irradiation on the densification behavior, microstructure, and microwave dielectric properties of low temperature sintering Al2O3 ceramics

The Fabrication of ZrO2–ZrC Microspheres by Internal Gelation and Carbothermal Reduction Process

Effects of Carbon Black on Microstructure and Mechanical Properties of Hot Pressed ZrB<sub>2</sub>-SiC Ceramics

Preparation of UN Microspheres by External Gelation

Preparation of Light-Weight Ceramic Microsphere by Dolomite and Gangue

Effects of Carbon Black on Microstructure and Mechanical Properties of Hot Pressed ZrB<sub>2</sub>-SiC Ceramics

Effect of CuO on the Burnability and Mineral Formation of High C3S Cement Clinker

Effect of CuO addition on the microstructure and electric properties of low-temperature sintered 0.25PMN-0.40PT-0.35PZ ceramics

Microstructure Evolution of (MgCoNiZnCu)O High Entropy Oxides Using Ceramic Injection Molding

Effect of Oxidative Stabilization on the Sintering of Mesocarbon Microbeads and A Study of Their Carbonization

Effect Of Sintering Process On Micro-structure And Properties Of Mullite Porous Ceramics Containing magnesium oxide

Effect of Al2O3on the Process Performance of ZrO2Microspheres

The Effect of Sintering Atmosphere and C/U on UCO Microspheres by Internal Gelation Process with Carbon Black

Fabrication Process Study of UCO Composite Ceramic Microspheres with Fructose As a Carbon Source by Internal Gelation and Carbothermic Reduction

The Effects of Carbon Content on ZrCO Microspheres Prepared by Internal Gelation Process with Carbon Black

The Study of Carbothermic Reduction–sintering of ZrO2–ZrC–C Composite Microspheres Prepared by Internal Gelation

Preparation of UCO Microspheres by Internal Gelation Process

Sintering of UO_2 Microsphere and Its Performance

Sintering of UO2 Microsphere and Its Performance

Effect of Carbon Powder on ZrC ZrO2 Microspheres Prepared by Internal Gelation Process

The Preparation of ZrO2–ZrC Ceramic Microspheres by Internal Gelation Process with Sucrose As a Carbon Source

Effect of UV irradiation on the densification behavior, microstructure, and microwave dielectric properties of low temperature sintering Al2O3 ceramics

The Fabrication of ZrO2–ZrC Microspheres by Internal Gelation and Carbothermal Reduction Process

Effects of Carbon Black on Microstructure and Mechanical Properties of Hot Pressed ZrB<sub>2</sub>-SiC Ceramics

Preparation of UN Microspheres by External Gelation

Preparation of Light-Weight Ceramic Microsphere by Dolomite and Gangue

Effects of Carbon Black on Microstructure and Mechanical Properties of Hot Pressed ZrB&lt;sub&gt;2&lt;/sub&gt;-SiC Ceramics

Effect of CuO on the Burnability and Mineral Formation of High C3S Cement Clinker

Effect of CuO addition on the microstructure and electric properties of low-temperature sintered 0.25PMN-0.40PT-0.35PZ ceramics

Microstructure Evolution of (MgCoNiZnCu)O High Entropy Oxides Using Ceramic Injection Molding

Effect of Oxidative Stabilization on the Sintering of Mesocarbon Microbeads and A Study of Their Carbonization

Effect Of Sintering Process On Micro-structure And Properties Of Mullite Porous Ceramics Containing magnesium oxide

Effect of Al2O3on the Process Performance of ZrO2Microspheres

Effects of Carbon Black on Microstructure and Mechanical Properties of Hot Pressed ZrB<sub>2</sub>-SiC Ceramics