Abstract:ZrO2 microspheres are widely used as a simulant of UO2 in the development of nuclear fuel. However, the cracking of ZrO2 microspheres prepared by internal gelation is still a challenge during drying and sintering processes. To address this issue, we designed and optimized the washing process for obtaining crack-free ZrO2 microspheres. Through thermogravimetric, infrared, Raman, BET, and SEM analysis, it is shown that the cracking of the microspheres is mainly related to the pores in microspheres. The washing solvent with low surface tension is used to reduce the effect of capillary force on pore shrinkage. Therefore, the optimal washing process was designed as trichloroethylene (TCE)-0.5 M NH3.H2O-Propylene glycol methyl ether (PM) and gel microspheres with a high specific surface area of 315.3 m(2)/g and pore volume of 0.4125 cm(3)/g were obtained. The characterizations also further showed that when the microspheres were dried and sintered, the water vapor and the decomposition gas of organic matter were completely released from the pores in the microspheres. Our new washing process could be directly extended for preparing crack-free ceramic microspheres by internal gelation.

Fabrication Process Study of UCO Composite Ceramic Microspheres with Fructose As a Carbon Source by Internal Gelation and Carbothermic Reduction

The Effect of Sintering Atmosphere and C/U on UCO Microspheres by Internal Gelation Process with Carbon Black

Sol–gel Preparation of ZrC–ZrO2 Composite Microspheres Using Fructose As a Carbon Source

The Preparation of ZrO2–ZrC Ceramic Microspheres by Internal Gelation Process with Sucrose As a Carbon Source

Preparation of UCO Microspheres by Internal Gelation Process

The Fabrication of ZrO2–ZrC Microspheres by Internal Gelation and Carbothermal Reduction Process

The Study of Carbothermic Reduction–sintering of ZrO2–ZrC–C Composite Microspheres Prepared by Internal Gelation

Fabrication of CeO2 by sol-gel process based on microfluidic technology as an analog preparation of ceramic nuclear fuel microspheres

Sintering of UO_2 Microsphere and Its Performance

Sintering of UO2 Microsphere and Its Performance

The Effects of Carbon Content on ZrCO Microspheres Prepared by Internal Gelation Process with Carbon Black

Preparation of Monodisperse ZrO2 Ceramic Microspheres (>200 Μm) by Co-Axial Capillary Microfluidic Device Assisted Internal Gelation Process

Controlled Synthesis of Porous FeCO3 Microspheres and the Conversion to Α-Fe2o3 with Unconventional Morphology

Fabrication of ceramic microspheres by diffusion-induced sol-gel reaction in double emulsions.

Fabrication And Characterization Of Zro2 Hollow Spheres

Microfluidic Fabrication of Ceramic Microspheres with Controlled Morphologies

Fabrication of Size-Controlled CeO2microparticles by a Microfluidic Sol–gel Process As an Analog Preparation of Ceramic Nuclear Fuel Particles

Fabrication and Properties of Porous Mullite Ceramics from Directly Sintering Ceramic Microspheres

The Effect of Washing Process on the Cracking of ZrO2 Microspheres by Internal Gelation

Fabrication and Characterization in Composites of Nanoenergetic Materials and Porous Metal with UV Ink Method

Microfluidic Fabrication of ZrO2 Microspheres Using Improved External Gelation Aided by Polyacrylamide Networks