Abstract:Electrochromic niobia (Nb205) coatings were prepared by the sot-gel spin-coating and d.c. magnetron sputtering techniques. Parameters were investigated for the process fabrication of sol-gel spin coated Nb205 films exhibiting high coloration efficiency comparable with that d.c. magnetron sputtered niobia films. X-ray diffraction studies (XRD) showed that the sot-gel deposited and magnetron sputtered films heat treated at temperatures below 450°C, were amorphous, whereas those heat treated at higher temperatures were slightly crystalline. X-ray photoelectron spectroscopy (XPS) studies showed that the stoichiometry of the films was Nb205. The refractive index and electrochromic coloration were found to depend on the preparation technique. Both films showed low absorption and high transparency in the visible range. We found that the n, k values of the sot-gel deposited films to be lower than for the sputtered films. The n and k values were n = 1.82 and k = 3 × 10−3, and n = 2.28 and k = 4 × 10−3 at 530 urn for sot-gel deposited and sputtered films, respectively. The electrochemical behavior and structural changes were investigated in 1 M LiC104/propylene carbonate solution. Using the electrochemical measurements and X-ray photoelectron spectroscopy, the probable electrode reaction with the lithiation and delithiation is Nb2O5 + x Li+ + x e− ↔ LixNb205. Cyclic voltametric (CV) measurements showed that both Nb205 films exhibits electrochemical reversibility beyond 1200 cycles without change in performance. “In situ” optical measurement revealed that those films exhibit an electrochromic effect in the spectral range 300 < λ < 2100 nm but remain unchanged in the infrared spectral range. The change in visible transmittance was 40% for 250 nm thick electrodes. Spectroelectrochemical measurements showed that spin coated films were essentially electrochemically equivalent to those prepared by d.c. magnetron sputter deposition.

Preparation and Optical Property of NbSiN Films

Optical and Mechanical Properties and Microstructures of Nb2O5, Ta2O5 and SiO2 Thin Films Prepared by Ion Beam Sputtering

Study on performance of Nb2O5 films with ion assisted deposition

Optical Properties Study of Silicon Oxynitride Films Deposited by RF Magnetron Sputtering

Characteristics of Nb2 O5 Thin Films Deposited by Ion Beam Sputtering

Preparation and Properties of NiO Films Via Sol-gel Process and Spin-coating

Influence of Sputtering Process on the Deposition and Optical Properties of Sicn Films

Thin films of silicon nitride deposited at room temperature by non-reactive magnetron sputtering: radiofrequency power and deposition time influence on the formation of α-Si3N4 and its optical properties

Preparation and Photoluminescence of Nanocrystalline Si-Rich Silicon Oxide Films by Pecvd

Optical and electrochemical characteristics of niobium oxide films prepared by sol-gel process and magnetron sputtering A comparison

Optical & Electronic Properties of Carbon Nitride Thin Films

Investigation of optical properties of silicon oxynitride films deposited by RF PECVD method

Ferroelectric SrxBa1-xNb2O6 optical waveguiding thin films on SiO2-coated Si(100) substrates

Microstructures and Optical Properties of SiNx Films

Atomic layer deposition and superconducting properties of NbSi films

Pulsed Laser Deposition of Optical Waveguiding LiNbO 3 Films on SiO 2 Substrate

MICROSTRUCTURE AND OPTICAL PROPERTIES OF SILICON NITRIDE THIN FILMS AS RADIATIVE COOLING MATERIALS

Growth and characterization of silicon nitride films for optoelectronics applications

Effects of C/Si ratios on structures and behaviors of NbSiCN nanocomposite films synthesized by reactive magnetron sputtering

Controlling the Superconducting Critical Temperature and Resistance of NbN Films through Thin Film Deposition and Annealing

SrxBa1-xNb2O6 optical waveguiding thin films on SiO2 coated Si(100) substrates