Abstract:Ti(C,N)-xCrMnFeCoNi-(15wt.%-x)Ni cermets (x = 0wt.%, 5wt.%, 10wt.%, 15wt.%) were fabricated by low-pressure sintering. Because of the sluggish diffusion effect of high-entropy alloy (HEA), the grain growth of cermets containing HEA binder is inhibited. The FCC binder phases of cermets with CrMnFeCoNi/Ni binders generate a uniform dispersion, motivating to form many complete and moderate rim phases and wet the ceramic particles. Furthermore, the hardness of cermets roughly increases, while the strength and fracture toughness maintain the change tendency of rising the peak and then falling with CrMnFeCoNi additions. Ti(C,N)-5wt.% CrMnFeCoNi-10wt.% Ni cermets obtains a prominent mechanical property combination with hardness of 1646 ± 13.5 HV30, strength of 2181 ± 167.2 MPa and fracture toughness of 9.1 ± 0.11 MPa m1/2. Besides, the cermets containing CrMnFeCoNi/Ni binders obtain reduced friction coefficients and low wear rates at 750 °C compared with Ti(C,N)–Ni cermets and Ti(C,N)-HEA cermets. The superior high-temperature wear resistance is ascribed to the thermal softening resistance of CrMnFeCoNi, strengthening and toughening effect of CrMnFeCoNi/Ni on matrix and the transition of wear mechanism from abrasive wear and the removal of tribochemical layers to the removal of tribochemical layers. The cutting lifetime of cermets containing CrMnFeCoNi/Ni binders is increased by 40%–70% in comparison with Ti(C,N)–Ni cermets during machining 17-4 PH stainless steel. Concisely, Ti(C,N)-based cermets with outstanding mechanical, wear resistance and cutting properties can be obtained by partially replacing Ni with 5–10 wt.% CrMnFeCoNi.

Fast Preparation of ZTA-TiC-FeCrNi Cermets by High-Gravity Combustion Synthesis

One-step Preparation of Dense TiC1 − Xnx–ni3ti Cermet by Combustion Synthesis

Addition Effect of ZrC Nano-powder on the Microstructure and Mechanical Properties of TiCN-based Cermets Prepared by Spark Plasma Sintering

In-situ Combustion Synthesis and Densification of TiC–xNi Cermets

Ultra-High Hardness TiC-W-Ni Cermets Prepared by Spark Plasma Sintering of Ultra-Fine TiC Powder

DENSE TiC-Al2O3-Fe CERMET FABRICATED BY SHS

Microstructure and Properties of Ti(C,N)-Based Cermets with AlxCoCrFeNiTi Binder

Enhanced Densification of Ultrafine Ti(C, N)-based Cermets Based on Grain-Growth Induced Liquid-Phase Pore Filling Mechanism

Fabrication, microstructure evolution, and mechanical properties of Ti(C,N)-HfN-WC-Ni-Mo cermets

TiC-Fe cermets fabricated by SHS

Evolution of microstructure and interfacial characteristics of complete solid-solution Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

Effects of CrMnFeCoNi additions on microstructure, mechanical properties and wear resistance of Ti(C,N)-based cermets

Synthesis of TiB 2 /Ti(C,N) cermet by RSPS: formation mechanism, shrinkage behavior, and mechanical properties

Research on TiC-Ni-Mo Composites by Combustion Synthesis

Effect of Fe on the Phases and Microstructure of TiC–Fe Cermets by Combustion Synthesis/quasi-Isostatic Pressing

Influence of TaC content on microstructure and mechanical performance of Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

Combustion synthesis and densification of large-scale TiC–xNi cermets

Thermite Synthesis of TiC/FeNiCr Cermet with Double-Layer Structure

Microstructure Transformation and Mechanical Properties of TiC–TiB2 Ceramics Prepared by Combustion Synthesis in High Gravity Field

Combustion Synthesis of TiB-Ti Cermets

Tuning microstructure for superb mechanical properties in a Ti(C,N)-(WMoTaNbTi)C-Ni/Co cermets via change sintering temperature