Abstract:Complete solid-solution Ti(C,N)-based cermet, with no typical core-rim structure, was synthesized through mechanical activation and subsequent in situ carbothermal reduction method. XRD, SEM, TEM, and C/N analysis were used to investigate the microstructure, phase transformation, and the interfacial characteristics of the present cermets. During solid-state sintering, the (Ti,Mo)C/(Ti,Mo)(C,N) phases formed through the transformation of Mo-based solid solution which generated by mechanical activation. Then, the formed (Ti,Mo)C/(Ti,Mo)(C,N) continuously dissolved into the nickel-based binder above 1100 °C. It was found that in the subsequent stage of liquid sintering, the mechanical activation and also the presence of extremely fine TiC/Ti(C,N) particles accelerated the Mo diffusion into the hard phase, resulting in a large quantity of (Ti,Mo)(C,N) solid solutions formed in the nickel-based binder. Finally, complete (Ti,Mo)(C,N) solid-solution phase was obtained via dissolution and re-precipitation. The higher toughness and transverse rupture strength (TRS) of the synthesized new cermet, as compared with traditional cermets, were mainly caused by the increased crack deflection and transgranular fracture of the novel cermets. Moreover, the interface among the Ni-based binder phase and complete solid solution hard phase exhibited a semi-coherency state with high-density dislocations, which also significantly improved the TRS and toughness of the synthesized cermets.

Thermite Synthesis of TiC/FeNiCr Cermet with Double-Layer Structure

Characterization and Formation Mechanisms of the TiC-Fe Cermet Layer in Ti-TiC-Fe Composites

Combustion synthesis and densification of large-scale TiC–xNi cermets

Synthesis of TiB 2 /Ti(C,N) cermet by RSPS: formation mechanism, shrinkage behavior, and mechanical properties

Evolution of microstructure and interfacial characteristics of complete solid-solution Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

Fast Preparation of ZTA-TiC-FeCrNi Cermets by High-Gravity Combustion Synthesis

The Formation of Ni-Mo Alloy Phase in Ticn-Based Cermets

Formation of Layer-Shaped Pores in TiC-Fe Cermet by Combustion Synthesis

One-step Preparation of Dense TiC1 − Xnx–ni3ti Cermet by Combustion Synthesis

Research on TiC-Ni-Mo Composites by Combustion Synthesis

Synthesis and characterization of Mo@Ni core-shell composite powder-reinforced (W,Ti)C-based cermet

Microstructure and Properties of Ti(C,N)-Based Cermets with AlxCoCrFeNiTi Binder

In-situ Combustion Synthesis and Densification of TiC–xNi Cermets

Microstructural evolution during combustion synthesis of TiC-Fe cermet

Effects of WC/TiC addition on the thermodynamic behavior of TiB 2 -based cermet during sintering process

Preparation, mechanical properties and enhanced wear resistance of TiC-Fe composite cermet coating

DENSE TiC-Al2O3-Fe CERMET FABRICATED BY SHS

Formation of solid solution structures in (Ti,W,Ta,Mo)(C,N) cermet via spark plasma sintering

Fabrication and Characterization of In-Situ Ti(C, N) - Cocrfeniti High Entropy Alloys Cermets

New TiC/Co 1.5 CrFeNi 1.5 Ti 0.5 Cermet with Slow TiC Coarsening During Sintering

Effect of Fe on the Phases and Microstructure of TiC–Fe Cermets by Combustion Synthesis/quasi-Isostatic Pressing