Abstract:In this paper, the effect of internal curing with pre-soaked lightweight aggregate (PSLWA) on shrinkage and interior relative humidity of four series concretes with compressive strength at 28 days around 30MPa, 60MP, 90MPa and 100MPa is investigated. The shrinkage induced cracking performance of concretes is evaluated with concrete-steel composite ring tests. The results show that the development of the internal relative humidity of concrete since casting exhibits first a vapor saturated stage (RH=100%, stage I), followed by gradually reducing stage (RH<100%, stage II). Under sealing, internal relative humidity at the center of the specimen for a given age is obviously decreased with increase of concrete strength. Under drying, similar internal relative humidity value is observed at 28 days for all concretes without internal curing. As PSLWA was added, the reduction rate on interior humidity in stage II is significantly decreased. But the efficiency on internal humidity rising is greatly influenced by concrete strength. The autogenous shrinkage is increased with increase of concrete strength. The drying shrinkage is decreased with increase of concrete strength. The total shrinkage of concrete is increased with increase of concrete strength. As PSLWA was added, the shrinkage reduction in both autogenous and drying shrinkages is obviously in high strength concretes, such as 90MPa and 100MPa concretes. The shrinkage reduction of internal curing on relatively low strength concrete, such 30MPa and 60MPa concrete is not obvious. Internal curing with PSLWA can greatly improve the shrinkage induced cracking performance. All concrete rings without internal curing are cracked under drying. The compressive strain in the steel ring at the concrete ring cracking is about 75 to 101 mu m/m. By contrast, the stable compressive strain at the inner steel ring for the concretes with internal curing becomes 10 to 40 mu m/m and no visible cracks were found on the specimens.

Shrinkage of Internal Cured High Strength Engineered Cementitious Composite with Pre-Wetted Sand-Like Zeolite

Influence of Zeolite Addition on Mechanical Performance and Shrinkage of High Strength Engineered Cementitious Composites

Mixture Optimization on Internally Cured High Strength Engineered Cementitious Composite with Pre-Wetted Sand-like Zeolite

Zeolite to Improve Strength-Shrinkage Performance of High-Strength Engineered Cementitious Composite

High-strength concrete mixture with calcined zeolite particles for shrinkage reduction

Unveil the Role of Nano-Caco3 in Early Shrinkage and Tensile Properties of Cement Paste: from Experimental Work to Modeling

Development of a Low-Shrinkage-Lightweight Engineered Cementitious Composite Based on Heavily Doped Zeolites

Effect of Pre-Wetted Zeolite Sands on the Autogenous Shrinkage and Strength of Ultra-High-Performance Concrete

Effective Solution for Low Shrinkage and Low Permeability of Normal Strength Concrete Using Calcined Zeolite Particles

Combination Effects of Internal Curing and Permanent Formwork on Shrinkage of High Strength Concrete

Effect of Water to Binder Ratio and Sand to Binder Ratio on Shrinkage and Mechanical Properties of High-strength Engineered Cementitious Composite

Efficient Utilization of Waste Marine Clay for Fine Aggregate to Develop Sustainable and Cost-Effective Strain-Hardening Cement-Based Composites

Enhancing the internal curing process of self-compacting concrete containing lightweight aggregate and chemical additives

Internal Curing Effect of Pre-Soaked Zeolite Sand on the Performance of Alkali-Activated Slag

Internal curing of high strength concrete based on saturated microporous cenospheres

Evaluation of Shrinkage Induced Cracking in Concrete with Impact of Internal Curing and Water to Cement Ratio

Shrinkage of High-Strength Calcium Sulfoaluminate Cement Concrete with Impact of Pre-Soaked Lightweight Aggregate Internal Curing

Influence of Pre-wetted Lightweight Aggregate on Early-age Shrinkage of High Strength Concrete

Interaction between zeolite and sulfate, and its influences on cement hydration

Mechanical Performance of Low Shrinkage Engineered Cementitious Composite in Tension and Compression

Integrative Study on the Effect of Internal Curing on Autogenous and Drying Shrinkage of High-Strength Concrete