Abstract:Creep rupture assessment is a significant issue in the field of high-temperature structural integrity. In this paper, the creep rupture assessment of 3D pressure pipelines with volumetric defects subjected to cyclic thermo-mechanical loadings is done using a direct numerical approach within the framework of stress compensation method (SCM). For calculation of creep rupture limit, an extended shakedown analysis scheme with yield strength correction is essentially performed, where the revised yield strength is determined as the minimum of the plastic yield strength and the creep rupture strength of material corresponding to a specified elevated temperature and rupture time. This direct numerical approach performs the creep rupture assessment by using the given creep rupture data of material rather than simulating the degenerative process of material based on creep damage constitutive equations under a specified loading history. The numerical approach is incorporated into commercial finite element software of Abaqus. Parametric studies on geometric dimensions of part-through slot affecting the creep rupture limit of 3D pressure pipelines with volumetric defects are conducted. Numerical results shown in this study indicate that the direct numerical approach accurately identifies the creep rupture limit boundary of the pressure pipeline, verified by the elastic-plastic cycle-by-cycle analysis. Failure mechanisms, such as local creep rupture, global creep rupture and global plastic rupture are detected under different loading combinations. These results give the helpful information for in-service integrity assessment of defective pressure pipelines at elevated temperature, and demonstrate the applicability and application prospect of the direct numerical approach in solving questions relevant to design or life assessment of other engineering structures.

Plastic Limit Analysis of Piping with Local Wall-Thinning under Elevated Temperature

Plastic Failure Analysis of Defective Pipes with Creep Damage under Multi-Loading Systems

Plastic Limit Analysis Of Modified 9cr-1mo Steel Pressure Vessel Containing Volume Defect With Creep Damage Law

Thermo-Mechanical Coupling Computation and Warping Analysis During Controlled-Cooling of X65 Heavy Pipeline-Plate

Creep Behaviors Calculated by Varying Material Constants Obtained from Different Stress Regions for a Closed-End P91 Pipe

Study on Creep Behavior and Fracture Life Prediction Method of P92 Steel Based on Finite Element Analysis

Plastic Collapse Analysis of Thin-Walled Pipes Based on Unified Yield Criterion

Numerical Limit Load Analysis of 3D Pressure Vessel with Volume Defect Considering Creep Damage Behavior

Theoretical Assessment of Burst Failure of Internally Pressurized Defect-Free Pipelines with Plastic Anisotropy

The Role of Initial Cracks on Creep Crack Growth and Fracture Mode of Thick-Walled Pressurized Pipe Weldments

Plastic Limit Load Analysis for Pressure Pipe with Incomplete Welding Defects Based on the Extended Net Section Collapse Criteria

Creep Rupture Assessment of Cyclically Heated 3D Pressure Pipelines with Volumetric Defects Using a Direct Numerical Approach

PLASTIC LIMIT LOAD ANALYSIS OF T-JUNCTIONS OF PIPING WITH LOCAL WALL-THINNINGS UNDER OUT-OF-PLANE MOMENT

Thermal-Mechanical Fatigue Behavior of P92 T-Piece Pipe

Plastic Limit Analysis of Defective Piping Systems

Plastic Limit Load Analysis of Pressure Pipes Containing Incomplete Welding Defects under Combined Loadings

Creep Fatigue Damage Assessment Of V-Butt Weld Pipe With An Extended Direct Steady Cycle Analysis

Thermal–mechanical Fatigue Behaviour of P92 T-piece and Y-piece Pipe

Plastic Limit Load Analysis of Defective Pipelines

An Insight into the Creep-Fatigue Damage Localization in Welded Joints Based on Crystal Plasticity Finite Element Method

Evaluation of creep damage of the steam pipelines with high temperature and high pressure