Abstract:The formation of silica on the coating surface is favorable to the oxidation protection of carbon fiber reinforced carbon matrix composites (C/C) or carbon fiber reinforced silicon carbide matrix composites (C/SiC) because the silica has a small diffusivity of oxygen and a certain ability to seal the coating cracks [1]. The metal positive ion dissolved in the silica can decrease the activation energy of non-intrinsic diffusion, and then it is unfavorable to the longterm oxidation protection [2]. As the oxidation protection coating with a thickness of about 150 µm, the extensive growth of CVD SiC is unstable [3-5]. Thus, it is impossible to remove preparation defects from the coating. Although the silica film formed on CVD SiC has an excellent oxidation resistance, it can not be used as a long-time coating. An outer layer is necessary to seal the defects of the CVD SiC coating. The outer layer should be completely dense and free of defects, and should be prepared by liquid method [6]. Silicon, having a lower melting point and an excellent oxidation resistance [7,8], is a moderate outer layer material, but it is difficult to prepare an uniform silicon coating with an adequate thickness. However, silicides formed during the liquid preparation makes the outer layer more uniform and thicker. Mixtures of silicon and another metal may give better materials for the outer layer. Zirconium can react rapidly with the melted silicon to form ZrSi2. With regard to the oxidation behavior of the ZrSi2, there are a few papers available exploring the oxidation of the Si/Zr binary system since 1970 [6]. It was reported that silica was formed at the ZrSi2-SiO2 interface due to good mobility of silicon in the silicide. Wei and Wu prepared a multi-layer coating of SiC-(Si/ZrSi2)-ZrSi2 on a C/C composite and studied the oxidation of the coated composite [9-10].

Dynamic Oxidation Resistance and Residual Mechanical Strength of ZrB2-CrSi2-SiC-Si/SiC Coated C/C Composites

Oxidation and Ablation Resistance of the ZrB2–CrSi2–Si/SiC Coating for C/C Composites at High Temperature

A ZrB2–SiC/SiC Oxidation Protective Dual-Layer Coating for Carbon/carbon Composites

Double Layer ZrSi2–ZrC–SiC/SiC Oxidation Protective Coating for Carbon/carbon Composites

Microstructure and Oxidation Behavior of C/C–ZrB2–SiC Composites Coated with SiC Coating at High Temperature

Oxidation Behavior and Microstructure Evolution of SiC-ZrB 2 -Zrc Coating for C/C Composites at 1673 K

A SiC–Si–ZrB2 Multiphase Oxidation Protective Ceramic Coating for SiC-coated Carbon/carbon Composites

A ZrSiO4/SiC Oxidation Protective Coating for Carbon/carbon Composites

SiC/SiC-ZrSi2 Coating with Micro-Pore to Protect C/C Composites Against Oxidation for Long-Life Service at High Temperatures

A Low-Temperature Preparation Strategy of SiC/ZrB2-CrSi2-Si/SiC Multilayer Oxidation-Resistant Coating for C/C Composites: Process, Kinetics and Mechanism Research

Preparation and Oxidation Property of ZrB2-MoSi2/SiC Coating on Carbon/carbon Composites

Oxidation and Ablation Resistance of ZrB2–SiC–Si/B-modified SiC Coating for Carbon/carbon Composites

Eliminated Siliconization Corrosion and Improved Oxidation Resistances of SiC-Si Coated C/C Composites Via a ZrB2-rich Transition Layer

A Novel Oxidation Protective SiC-ZrB2-ZrSi2 Coating with Mosaic Structure for Carbon/carbon Composites

SiC-MoSi_2/ZrO_2-MoSi_2 coating to protect C/C composites against oxidation

Oxidation Protection and Behavior of In-Situ Zirconium Diboride–silicon Carbide Coating for Carbon/carbon Composites

Sic-Si-Zrsio4 Multiphase Oxidation Protective Coating for Carbon/Carbon Composites

Oxidation Behaviour of C/SiC Composites with a Si‐Zr Coating from Room Temperature to 1500 °C

Anti-oxidation properties of ZrB2 modified silicon-based multilayer coating for carbon/carbon composites at high temperatures

A dense ZrB2-SiC-Si/SiC-Si coating to protect carbon/carbon composites against oxidation at 1773 K and 1973 K

Preparation and oxidation kinetics of SiC/ZrO2-SiO2 oxidation protective coating for carbon-carbon composites