Abstract:In order to improve the oxidation resistance of carbon/carbon (C/C) composites, a ZrSiO4 coating on SiC pre-coated C/C composites was prepared by a hydrothermal electrophoretic deposition process. Phase compositions and microstructures of the as-prepared ZrSiO4/SiC coating were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectrometer (EDS). The anti-oxidation property and failure mechanism of the multi-layer coating were investigated. Results show that hydrothermal electrophoretic deposition is an effective route to prepare crack-free ZrSiO4 outer coatings. The multi-layer coating obviously exhibits two-layer structure. The inner layer is composed of SiC phase and the outer layer is composed of ZrSiO4 phase. The bonding strength between the outer layer coatings and C/C–SiC substrate are 30.38 MPa. The ZrSiO4/SiC coating displays excellent oxidation resistance and can protect C/C composites from oxidation at 1773 K for 332 h with a mass loss rate of only 0.48 × 10− 4 g/cm2·h. The mechanical properties of the specimens are 84.36 MPa before oxidation and 68.29 MPa after oxidation. The corresponding high temperature oxidation activation energy of the coated C/C composites at 1573–1773 K is calculated to be 119.8 kJ/mol. The oxidation process is predominantly controlled by the diffusion rate of oxygen through the ZrSiO4/SiC multi-coating. The failure of the coating is due to the formation of penetrative holes between the SiC bonding layer and the C/C matrix at 1773 K.

Sic-Si-Zrsio4 Multiphase Oxidation Protective Coating for Carbon/Carbon Composites

A SiC–Si–ZrB2 Multiphase Oxidation Protective Ceramic Coating for SiC-coated Carbon/carbon Composites

A ZrSiO4/SiC Oxidation Protective Coating for Carbon/carbon Composites

SiC-MoSi_2/ZrO_2-MoSi_2 coating to protect C/C composites against oxidation

A ZrB2–SiC/SiC Oxidation Protective Dual-Layer Coating for Carbon/carbon Composites

An Oxidation Protective Si-Mo-Cr Coating for C/Sic Coated Carbon/Carbon Composites

A Novel Oxidation Protective SiC-ZrB2-ZrSi2 Coating with Mosaic Structure for Carbon/carbon Composites

C/SiC/Si-Mo-B/glass multilayer oxidation protective coating for carbon/carbon composites

SiC-Si Coating with Micro-Pores to Protect Carbon/carbon Composites Against Oxidation

Preparation and oxidation kinetics of SiC/ZrO2-SiO2 oxidation protective coating for carbon-carbon composites

C/SiC/Si-Mo-Cr multilayer coating for carbon/carbon composites for oxidation protection

Oxidation Protective C/SiC/Si-SiC Multilayer Coating for Carbon/Carbon Composites Applying at 1873 K

C/SiC/MoSi2-Si multilayer coatings for carbon/carbon composites for protection against oxidation

High Performance SiC Oxidation Protective Coating with ZrO2 Particle Dispersion for Carbon/Carbon Composites

C/SiC/MoSi2–SiC–Si Multilayer Coating for Oxidation Protection of Carbon/carbon Composites

Si-Mo-Cr coating for C/SiC coated carbon/carbon composites against oxidation

Mullite-Al2O3-SiC Oxidation Protective Coating for Carbon/carbon Composites

SiC/SiC-ZrSi2 Coating with Micro-Pore to Protect C/C Composites Against Oxidation for Long-Life Service at High Temperatures

Double Layer ZrSi2–ZrC–SiC/SiC Oxidation Protective Coating for Carbon/carbon Composites

A Si–SiC Oxidation Protective Coating for Carbon/carbon Composites Prepared by a Two-Step Pack Cementation

Preparation and Anti-Oxidation Property of Sic/Sic-Mosi2 Coating on C/C Composite