Abstract:In order to improve the high temperature oxidation and ablation resistance of C/C composites, ZrB2-ZrC-SiC ultra-high temperature composite ceramic coatings were prepared on C/C composites by laser cladding using Zr, B4C, and Si as raw materials. The microstructure of the coating was characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD). Air isothermal oxidation (1600 °C, 80 min) and oxyacetylene flame ablation (2400 kW/m2, 300 s) were used to evaluate the high-temperature oxidation and ablation properties of the coating, respectively. The results show that the microstructure of laser cladding coating is a totem of black and white. The white part is mainly the first solidified high melting point ZrB2 phase, and the black part is the latter solidified eutectic structure, which is mainly composed of ZrB2(ZrB12)-ZrC or ZrB2(ZrB12)-SiC two phases. After oxidation at 1600 °C and 80 min, the coating is mainly composed of ZrO2 and ZrSiO4 phases, and ZrSiO4 is basically distributed among ZrO2 particles. The high temperature oxidation and ablation properties of the coating are better than the C/C composite matrix, and the mass ablation rate of the coating is about 1/4 of the latter.

Oxidation Behavior and Microstructure Evolution of SiC-ZrB 2 -Zrc Coating for C/C Composites at 1673 K

Microstructure and oxidation behavior of SiOC coatings on C/C composites co-deposited with HMDS and TEOS by using CVD process

A dense ZrB2-SiC-Si/SiC-Si coating to protect carbon/carbon composites against oxidation at 1773 K and 1973 K

Formation and Oxidation Behavior of Mo-Si-B Composite Coatings with B-rich Interlayer Prepared by Slurry Sintering Method

ZrB2 particles reinforced glass coating for oxidation protection of carbon/carbon composites

Effect of Lu2O3 addition on the oxidation behavior of SiC-ZrB2 composite coating at 1500 °C: Experimental and theoretical study

A gradient composite coating to protect SiC-coated C/C composites against oxidation at mid and high temperature for long-life service

High temperature oxidation resistance of Y2O3 modified ZrB2-SiC coating for carbon/carbon composites

An oxidation protective coating prepared by SiC densifying HfB2-SiC skeleton for SiC-coated C/C composites at 1473, 1773, and 1973 K

Effect of the Y2O3 amount on the oxidation behavior of ZrB2-SiC-based coatings for carbon/carbon composites

Deposition voltages on the phase evolutions, microstructures, and oxidation behaviors of thermal-resistance Glass-MoSi2-SiC coating

Effect of boronizing treatment on the oxidation resistance of Zr2(AlSi)4C5/SiC composite

Isothermal Oxidation of Zr2[Al(Si)]4C5–SiC Composites at 1000–1300°C in Air

ZrSi2-SiC/SiC Anti-Oxidant Coatings Prepared on Graphite Spheres by Two-Step Pack Cementation Process

Oxidation protection of tri‐layer La2Zr2O7/Yb2Si2O7/SiC‐coated Cf/SiC composites at high temperature

Effect of silicon/graphite ratio and temperature on oxidation protective properties of SiC/ZrB2–SiC coatings prepared by pack cementation

Experimental and first-principles simulation study on oxidation behavior at 1700 °C of Lu2O3–SiC-HfB2 ternary coating for SiC coated carbon/carbon composites

Oxygen barrier capability of ZrB2-SiC coating at 1700 °C strengthened by film-forming treatment

Effect of the ZrB2 content on the oxygen blocking ability of ZrB2-SiC coating at 1973K

A Thick SiC-Si Coating Prepared by One-Step Pack Cementation for Long-Term Protection of Carbon/carbon Composites Against Oxidation at 1773 K

High Temperature Oxidation and Oxyacetylene Ablation Properties of ZrB2-ZrC-SiC Ultra-High Temperature Composite Ceramic Coatings Deposited on C/C Composites by Laser Cladding