Abstract:MgB2 ultrathin films have been recently recognized to have potential for making sensitive superconducting devices working at relatively high temperatures. Investigation on the stability of MgB2 ultrathin films under various environmental conditions should be helpful in evaluating their prospect in practical device applications. Here, we present a comparative study on the degradation of MgB2 films of thicknesses of similar to 15 nm grown by hybrid physical-chemical vapor deposition method and then placed at room temperature under three different kinds of environments, i.e., in air, in a desiccator with reduced humidity, and in a vacuum chamber with further reduced atmospheric pressure. The study was performed by measuring the normal-state resistance and the superconducting properties such as the superconducting critical temperature T-c and the upper critical field H-c2 of the films after different storage times, in conjunction with supplemental scanning electron microscopy and X-ray diffraction measurements. It has been found that, compared with the film exposed to air that started to show apparent degradation when the storage time was beyond about one month, the films kept in a desiccator or low vacuum exhibited less degradation. In particular, the film in low vacuum remained stable throughout the measured time period of similar to 4 months. The results suggest that the degradation of MgB2 ultrathin films in ambient environment may mainly arise from the interaction of the sample with the moisture in the air and that, in a dry air or preferably vacuum or an N-2 environment, MgB2 ultrathin films can maintain the reasonable long-time stability for superconducting applications.

Protection of BN for MgB 2 Films Against Degradation in Water

Degradation of MgB 2 Ultrathin Films under Different Environmental Conditions

The study of MgB2/BN/MgB2 trilayer films

Film Fabrication and Electronic Devices of MgB2 Superconductor

MgB2 Thick Films on Three-Dimensional Structures Fabricated by HPCVD

Electron Microscopic Analysis of Josephson Junction of Mgb2 Superconducting Material with High Critical Temperature

Dielectric Barrier Discharge Assisted Chemical Vapor Deposition of Boron Nitride Phosphide Films on A Quartz Substrate

GROWTH AND PROPERTIES OF SUPERCONDUCTING MgB_2 THIN FILM FABRICATED ON Al_2O_3 SUBSTRATE BY HYBRID PHYSICAL CHEMICAL VAPOR DEPOSITION

Thickness Dependenceof Superconducting Properties of MgB2 THIN FILMS on Al2O3 Substrates

Biaxial Strain Engineering on the Superconducting Properties of MgB2 Monolayer

A Study on the Components of MgB2 Thick Film Prepared Via HPCVD

SUPERCONDUCTING MgB2 FILMS VIA EX-SITU ANNEALING UNDER DIFFERENT Ar PRESSURE PREPARED BY E-BEAM EVAPORATION

Effect of thickness on properties of MgB2 thin films

Fabrication of superconducting magnesium diboride thin films by electron beam annealing

Clean Mgb2 Thin Films On Different Types Single-Crystal Substrate Fabricated By Hybrid Physical-Chemical Vapor Deposition

MgB2 superconductor thin films on Si and Al2O3 substrates

Hybrid Physical-Chemical Vapor Deposition of Ultrathin Mgb2 Films on Mgo Substrate with High T-C and J(C)

Superconducting Mgb2 Thin Films On Silicon Carbide Substrates By Hybrid Physical-Chemical Vapor Deposition

Superconducting MgB 2 film prepared by chemical vapor deposition at atmospheric pressure of N 2

HPCVD Thin Film MgB2 for Superconducting Magnetic Shielding