Abstract:Prior to practical service, hot-section components (e.g. airfoils and vanes) of a gas turbine engine are necessarily coated by a protective metallic coating (such as aluminidi diffusion coating, modified aluminide coating and MCrAlY overlay etc.) to resist high temperature oxidation and hot corrosion. Among the modified aluminide coatings, the coating with Pt-modification has attracted great attention and is widely used in applications requiring high reliability and extended service life since it possesses superior oxidation/corrosion resistance at high temperature. The presence of Pt in aluminide coating is favorable for increasing bonding strength of oxide scale, enlarging phase region of beta 3-NiAI and confining detrimental effect of sulphur etc. Although Pt-modification has exhibited visible benefits for acquiring better high-temperature performance, it is far from satisfaction to develop an ideal aluminide diffusion coating. Reactive elements such as Y, Hf, Zr or their oxides have been employed to modify the nickel aluminide coating system, with an aim to further improve scale adhesion and promote exclusive formation of alpha-Al2O3 simultaneously. In this work, a Zr-doped PtAl2+(Ni, Pt)Al dual-phase aluminide coating was prepared on a Ni-based single crystal superalloy by co-deposition of Pt-Zr through electroplating and sub-sequent aluminization treatments The coating was mainly composed of three layers: the outmost layer consisted of double phases with PtAl2 particles dispersed in beta-(Ni, Pt)Al domain, while the interlayer comprised beta-(Ni, Pt)Al with small amount of Cr-precipitates, and the bottom layer was an inter-diffusion zone (IDZ). Zirconium was mainly distributed inside beta-(Ni, Pt)Al solid solution in both the outmost layer and the interlayer. Compared with normal PtAl2+(Ni, Pt)Al dual-phase coating, the hot corrosion behavior of the Zr-doped PtAl2 + (Ni, Pt)Al coating was assessed in a salt mixture of Na2SO4/NaCI (75:25, mass ratio) at 850 degrees C in static air. The results indicated that the Zr-doped PtAl2+(Ni, Pt)Al dual-phase coating exhibited superior hot corrosion resistance since Zr was confirmed able to capture and fix S and CI to diminish their detrimental effects. Meanwhile, a pre-oxidation treatment did not effectively improve the overall hot corrosion resistance of normal PtAl2+(Ni, Pt)Al coating because the thin alumina scale formed during pre-oxidation was unable to prohibit the sustained inward-invasion of the mixed salt.

Preparation and Enhanced Oxidation Performance of a Hf-doped Single-Phase Pt-modified Aluminide Coating

Synergistic Effect of Pt and Hf on the Early-Stage Oxidation Behaviour of NiAl Coating at 1000°C

Co-doping Effect of Hf and Y on Improving Cyclic Oxidation Behavior of (ni,pt)al Coating at 1150 °C

Cyclic Oxidation Behaviour of Pt-doped Aluminide Coating on DZ125 Containing Hf

Effect of Hf Addition on Initial Microstructure of (ni, Pt)Al Coating and Inhibiting the Detrimental Sulfur During High Temperature Exposure at 1150 °C

Microstructure and Cyclic Oxidation of a Hf-doped (ni,pt)al Coating for Single-Crystal Superalloys

Oxidation Performance and Interdiffusion Behavior of a Pt-Modified Aluminide Coating with Pre-deposition of Ni

Cyclic oxidation behavior of Pt modified NiCoCrAlYHfZr + AlNiY coating on a Ni-based single crystal superalloy

Preparation and Enhanced Hot Corrosion Resistance of a Zr-Doped PtAl2+(Ni, Pt)Al Dual-Phase Coating

Preparation and oxidation performance of a low-diffusion Pt-modified aluminide coating with Re-base diffusion barrier

High-temperature performance of Pt-modified Ni-20Co-28Cr-10Al-0.5Y coating: Formation mechanism of Pt-rich overlayer and its effect on thermally grown oxide failure

Pt-modification on the thermal cycling behavior of NiCoCrAlYTa coating: a case study

Oxidation Behavior and Oxide Transformation of a Pt-Modified Aluminide Coating at Moderate High Temperature

Effects of coating growth mode on the oxidation behavior of a hybrid Pt/Ru-modified aluminide coating at 1200 °C

A Zr-doped single-phase Pt-modified aluminide coating and the enhanced hot corrosion resistance

Oxidation Property and Failure Mechanism of A Single Phase Ptal2 Coating

Hot Corrosion and Cyclic Oxidation Performance of a Ptal2-Dispersed (ni,pt)al Coating Prepared by Low-Activity High-Temperature Aluminizing

Enhancing the High-Temperature Corrosion Resistance of HVOF-sprayed NiCoCrAlY Coating in Marine Environment by Pt Modification and Pre-Oxidation

Effect of aluminisation characteristics on the microstructure of single phase β-(Ni,Pt)Al coating and the isothermal oxidation behaviour

Investigation on the microstructural evolution and oxidation resistance of Ru-doped NiAlHf coatings at 1200 °C

Preparation and Enhanced Isothermal Oxidation Resistance of a Low Diffusivity NiRePtAl Single-Phase Coating