Abstract:Ultra-high performance glass sand concrete (UHPGC) is a new composite material with superior mechanical properties and durability made by replacing quartz sand in traditional ultra-high performance concrete (UHPC) with environmentally friendly and economical glass sand recycled from waste glass. This study investigated the flexural and fracture characteristics of UHPGC notched beams with prefabricated notches at three different locations (mid-span, 100 mm off mid-span and 145 mm off mid-span) using four-point bending tests. Meanwhile, the damage evolution processes of notched beams under flexural load were monitored in real time and characterized by acoustic emission (AE) technology. Fracture modes were automatically classified based on Gaussian mixture model (GMM) and support vector machine (SVM) of rise angle (RA) and average frequency (AF). Outlier analysis of b -value were applied to provide a warning prior to complete failure of UHPGC notched specimen. The results revealed that notched position presents significant effects on flexural strength, flexural toughness and fracture energy, and exhibit considerable influence on AE parameters and cracking patterns. The farther the notch is away from the mid-span, the greater the flexural strength, flexural toughness and fracture energy exhibit due to the weakened stress concentration. As it takes longer to gather enough strain energy at the tip of the notch to crack, AE monitoring shows that higher amplitude and hysteretic nature of AE parameters such as accumulated energy and information entropy, etc., can be recorded as notch position away from the mid-span. The farther the notch is away from mid-span, the more shear cracks predominate at the later stages of damage. Cumulative AE energy and fracture energy throughout the damage process are found to exhibit a favorable exponential relationship. In addition, the b -value outlier analysis can provide failure warning for UHPGC notched beams. This study is of great significance in exploring the fracture behavior of UHPGC and providing reference for engineering applications related to UHPGC failure.

In-depth Analysis of Notched 3-P-b Concrete Fracture

Fracture Toughness of Ordinary Plain Concrete Under Three-Point Bending Based on Double-K and Boundary Effect Fracture Models

A Weibull distribution-based method for the analysis of concrete fracture

Influence of Mineral Admixture on Early-Age Concrete Cracking

Fracture Toughness And Microstructure Of Concrete At Early-Ages

A Quasi-2D Exploration of Mixed-Mode Fracture Propagation in Concrete Semi-Circular Chevron-Notched Disks

Experimental study on fracture properties of self-compacting concrete

Evaluation of Fracture Parameters of Concrete from Bending Test Using Inverse Analysis Approach

Research on the Fracture Behavior of Steel-Fiber-Reinforced High-Strength Concrete

Fracture parametric study on cement-based materials from three-point bending test

Fracture of 0.1 and 2 M Long Mortar Beams under Three-Point-bending

Numerical simulation of cracking of early-age concrete three-point beams

Dynamic Fracture Catastrophe Model of Concrete Beam under Static Load

Experimental Investigation On Mode Ii Fracture Toughness K-Iic Of Concrete And Fracture Behavior

STUDY ON FRACTURE PROCESS OF CONCRETE THREE-POINT BENDING BEAMS RETROFITTED WITH UHTCC

Experimental Investigation on Mode II Fracture Toughness K<sub>IIC</sub> of Concrete and Fracture Behavior

Mesoscale fracture analysis of three-point bending concrete beams based on cohesive zone model

Assessment of Fracture Toughness Using Small Punch Tests of Prenotched Specimens

Determination of Concrete Fracture Parameters from a Three-Point Bending Test

Effect of Notch Location on Flexural and Fracture Behaviors of UHPGC Notched Beam Based on Four-point Bending Test and Acoustic Emission Monitoring

Experimental study on fracture toughness K_(Ⅱc) of concrete