Abstract:The Bi 2 Sr 2 CaCu 2 O x (Bi-2212) precursor powder has been successfully synthesized using the spray pyrolysis method, and the powder has also been made into high critical current density Bi-2212/Ag-alloy wire with 666 filaments through the oxide-powder-in-tube (PIT) and the partial-melt processing (PMP). The advantage of low segregation was found in the spray pyrolysis precursor powder due to the gas-film-barrier high-temperature calcination for the micro-sized atomized solution droplets during the spray pyrolysis process. The droplets are instantly transformed into nearly nano-sized spherical oxide powder, and the liquid phase segregation could only appear inside each of these powder spheres during the process. And the elemental content and elemental distribution in each droplet are perfectly uniform, improving the homogeneity of the final oxide powder. In conventional precursor powders that have only undergone a solid phase sintering, the liquid phase flows between the powders, resulting in severe segregation. As the segregation phenomenon was almost avoided, the content of the Bi 2 Sr 2 CuO x (Bi-2201) phase and (Sr, Ca) x Cu y O z (alkaline earth cuprates, AEC) phase in the precursor powder decreased, leading to the enhancement of the Bi-2212 content in the precursor powder and the conductive characteristics of the wire. The superconducting critical transition temperature T c of the final wire is 90.53 K, and the Δ T c value is only 0.08 K. The wire has a small Δ T c value, further indicating the higher purity of the superconducting sample. The critical current density ( J c ) of the Bi-2212 wire reaches 283 A/mm 2 at 65 K in self-field, which is higher than that of the wire reported in the literature. After high-pressure heat treatment, the highest J e and the highest J c of the wires reach 538 A/mm 2 and 2987 A/mm 2 at 4.2 K & 12T. It indicated that the spray pyrolysis method would be a candidate method for preparing high-performance Bi-2212 wire.

Preparation And Characterization Of Large-Quantity Bi-2223 Precursor Powder By Oxalate Coprecipitation

Preparation of Bi-Based Superconductor Precursor Powder by a Spray- Dry+ Fluidized Bed Denitration Technology

PREPARATION OF NANOSIZED Bi3.25 La0.75 Ti3 O12 POWDER BY COPRECIPITATION METHOD

Study on Phase-Formation Mechanism and Intergrowth for Bi(Pb)-Sr-Ca-Cu-O System

Preparation of 110k Superconductor in Bi-Sr-Ca-Cu-O System

Preparation of high-performance high temperature superconducting Bi-2212 wires by the spray pyrolysis powder

Preparation and Superconductivity of Bi3PbCa3Sr3Cu4Oy

Synthesis of (Bi,Pb)-2223 superconductor powder by pechini method

The reaction process of the Bi-Sr-Ca-Cu-O system and the forming mechanism of the 2212 superconducting phase

Optimization of a New Modified Wet-Chemistry Process for the Synthesis of BPSCCO Superconductor Precursor Powders with Specific Stoichiometr

PREPARATION AND SINTERING PROPERTIES OF BaTi4O9 BY CITRIC ACID GEL METHOD

Effects of Heat Treatment Temperature on Phase Formation and Properties of Bi-2212 Spray Pyrolysis Powder

Formation Mechanism of the 3321 Phase in Bi-System High Temperature Superconduting Materials

Performance Evaluation Of(bi,pb)2sr2ca2cu3ox Superconducting Precursor Powder by Analysis of Oxygen Partial Pressure

Bismuth–iron-based precursor: preparation, phase composition, and two methods of thermal treatment

Preparation and Superconductivity of the High-Tc Phase of Pb-doped Bi-Sr-Ca-Cu-O Superconductor

The influences of powder processing variables on the properties of Bi-2223/Ag tapes

A process for the preparation of high-quality and uniform large-scale Bi2212 superconducting films via the sol-gel method

Preparation and Characterization of A New Single Crystal Bi2sr1.5pr2.5cu2oy

Effect of Lead Oxide Compounds on the Microstructure and Properties of Bi-2223/Ag Tapes

The evolution of Bi-2223 phase and liquid phase during the first heat treatment in Bi-2223/Ag superconducting tapes