Formation Mechanism of High T-C Superconduting Phase Yba2cu3o7-Delta
Tang Youqi,Zhang Yufen,Zheng Xiangmiao,Wei Chengquian,Lin Bingxiong
DOI: https://doi.org/10.3866/pku.whxb19880303
1988-01-01
Acta Physico-Chimica Sinica
Abstract:The Y-Ba-Cu mixed oxide system is obtained when any kinds of materials containing Y, Ba, Cu are heated at 850 degrees C, when, heated to 900 degrees C, an oxygen-rich tetragonal phase I (YBa2Cu3O6.8) is formed. At 930 degrees C an oxygen deficient tetragonal phase,11 (YBa2Cu3O6) appears, and the oxygons at positions (1/2, 0,0) and (0,1/2,0) are almost drived out,The oxygen absorbed above 850 degrees C are equally distributed onto (1/2,0,0) and (0,1/2 0), the amount of which varies with tem perature, It is absorbed oxygen that migrates easily from (0,1/2,0) to (1/2,0,0)as the tetragonal phase transits into the orthorhomtic phase at 650 degrees C, which makes differences in oxygen-ocupancy at these two positions, such that the structure deviates from tetragonality and the superconduting properties are improved.